A study on stress corrosion cracking and hydrogen embrittlement of Jethete M152 martensitic stainless steel
作者： Sicong Shen , Xiaolong Song , Qizhen Li , Xinfeng Li , Ruihua Zhu
DOI: 10.1016/J.MSEA.2018.10.091
关键词:
摘要: … factor in stress corrosion cracking and hydrogen embrittlement for Jethete M152 steel. Meanwhile, it is beneficial to enhance resistance to stress corrosion cracking and hydrogen …
sci-hub.se 参考文章(36)
G. M. Pressouyre, A classification of hydrogen traps in steel Metallurgical Transactions A. ,vol. 10, pp. 1571- 1573 ,(1979) , 10.1007/BF02812023
Julien Deleume, Jean-Marc Cloué, Eric Andrieu, Influence of δ phase precipitation on the stress corrosion cracking resistance of alloy 718 in PWR primary water Journal of Nuclear Materials. ,vol. 382, pp. 70- 75 ,(2008) , 10.1016/J.JNUCMAT.2008.09.018
Y.S. Ding, L.W. Tsay, M.F. Chiang, C. Chen, Gaseous hydrogen embrittlement of PH 13-8 Mo steel Journal of Nuclear Materials. ,vol. 385, pp. 538- 544 ,(2009) , 10.1016/J.JNUCMAT.2008.12.048
W.C. Chiang, C.C. Pu, B.L. Yu, J.K. Wu, Hydrogen susceptibility of 17-4 PH stainless steel Materials Letters. ,vol. 57, pp. 2485- 2488 ,(2003) , 10.1016/S0167-577X(02)01298-3
Ernesto Villalba, Andrej Atrens, Hydrogen embrittlement and rock bolt stress corrosion cracking Engineering Failure Analysis. ,vol. 16, pp. 164- 175 ,(2009) , 10.1016/J.ENGFAILANAL.2008.01.004
R.L. Higginson, C.L. Verona, Stress corrosion cracking of CrNi martensitic stainless steels for steam turbine blades Materials at High Temperatures. ,vol. 26, pp. 79- 83 ,(2009) , 10.3184/096034009X438202
S. Bechtle, M. Kumar, B.P. Somerday, M.E. Launey, R.O. Ritchie, Grain-boundary engineering markedly reduces susceptibility to intergranular hydrogen embrittlement in metallic materials Acta Materialia. ,vol. 57, pp. 4148- 4157 ,(2009) , 10.1016/J.ACTAMAT.2009.05.012
Hyojin Kim, Yongho Kang, Crack evaluation and subsequent solution of the last stage blade in a low-pressure steam turbine Engineering Failure Analysis. ,vol. 17, pp. 1397- 1403 ,(2010) , 10.1016/J.ENGFAILANAL.2010.04.005
R.M. Schroeder, I.L. Müller, Stress corrosion cracking and hydrogen embrittlement susceptibility of an eutectoid steel employed in prestressed concrete Corrosion Science. ,vol. 45, pp. 1969- 1983 ,(2003) , 10.1016/S0010-938X(03)00035-0
ZY Liu, XG Li, CW Du, L Lu, YR Zhang, YF Cheng, None, Effect of inclusions on initiation of stress corrosion cracks in X70 pipeline steel in an acidic soil environment Corrosion Science. ,vol. 51, pp. 895- 900 ,(2009) , 10.1016/J.CORSCI.2009.01.007