摘要: The constitution and properties of crazes in glassy polymers their relation to crack propagation are reviewed. New evidence is discussed which shows the craze be much softer than parent polymer but capable sustaining large stresses strains up point failure. Craze failure more dependent on molecular weight formation, this difference reflected changes both fracture surface morphology toughness with weight. Finally mechanical thought integrally related behavior high impact plastics.