Anomalous properties of in-situ-produced silver-copper composite wires I. Electrical conductivity

摘要: The silver and copper crystals of an eutectic Ag-Cu alloy (71.9 wt% Ag) get a fibre-like shape by wire drawing after high degree deformation. extremely thin fibres attain diameter about 100 A at reduction cross section η = 99.99%. Such in-situ-produced silver-copper composite wires show extensive anomalies the conduction phenomena due to size effect. Especially, interaction fibre interfaces with electrons causes extraordinary decrease electrical conductivity. This anomalous change resistivity as function can be explained free-path theory electrons. mean free paths well their scattering factors were determined different test temperatures. measured values are in good agreement calculated ones, obtained strict theory. Die Silber- und Kupferkristalle der eutektischen Ag-Cu-Legierung (71,9 Gew% werden nach hohen Formanderungen durch Drahtziehen zu feinen Fasern ausgezogen. Bei den grosten erreichbaren Querschnittsabnahmen von 99,99% erreichen die extrem dunnen Kupferfasern Durchmesser etwa A. Diese in-situ erzeugten Silber-Kupfer-Verbunddrahte zeigen ausgepragte Anomalien Leitungsphanomene, auf dem Size-Effekt beruhen. Insbesondere ruft Wechselwirkung Fasergrenzflachen mit Leitungselektronen eine ausergewohnliche Abnahme elektrischen Leitfahigkeit hervor. Die anomale Widerstandsanderung Abhangigkeit vom wird Hilfe Weglangentheorie beschrieben. mittlere frcie Weglange Silber Kupfer sowie entsprechenden Streufaktoren wurden fur verschiedene Versuchstemperaturen bestimmt. gemessenen Werte stehen guter ubereinstimmung exakten Theorie berechneten Grosen.