Isothermal oxidation behavior of cryomilled NiCrAlY bond coat: Homogeneity and growth rate of TGO
作者： Kaka Ma , Julie M. Schoenung
DOI: 10.1016/J.SURFCOAT.2011.05.025
关键词:
摘要: … The initial TGO growth follows parabolic growth kinetics in both systems, but … TGO thickness, thinner TGO layers after long-term exposure, slower TGO growth rate, and uniformity in TGO …
elsevier.com
sci-hub.se 参考文章(54)
H. E. Evans, M. P. Taylor, Diffusion Cells and Chemical Failure of MCrAlY Bond Coats in Thermal-Barrier Coating Systems Oxidation of Metals. ,vol. 55, pp. 17- 34 ,(2001) , 10.1023/A:1010369024142
P. Niranatlumpong, C. B. Ponton, H. E. Evans, The Failure of Protective Oxides on Plasma-Sprayed NiCrAlY Overlay Coatings Oxidation of Metals. ,vol. 53, pp. 241- 258 ,(2000) , 10.1023/A:1004549219013
W BALLUFFI ROBERT, M ALLEN SAMUEL, W CARTER CRAIG, None, Kinetics of materials ,(2005)
D.R.G. Achar, R. Munoz-Arroyo, L. Singheiser, W.J. Quadakkers, Modelling of phase equilibria in MCrAlY coating systems Surface & Coatings Technology. ,vol. 187, pp. 272- 283 ,(2004) , 10.1016/J.SURFCOAT.2004.02.018
A.G. Evans, D.R. Clarke, C.G. Levi, The influence of oxides on the performance of advanced gas turbines Journal of The European Ceramic Society. ,vol. 28, pp. 1405- 1419 ,(2008) , 10.1016/J.JEURCERAMSOC.2007.12.023
T.A. Taylor, P.N. Walsh, Dilatometer studies of NiCrAlY coatings Surface & Coatings Technology. pp. 41- 48 ,(2004) , 10.1016/J.SURFCOAT.2004.08.003
Feng Tang, Leonardo Ajdelsztajn, Julie M. Schoenung, Characterization of oxide scales formed on HVOF NiCrAlY coatings with various oxygen contents introduced during thermal spraying Scripta Materialia. ,vol. 51, pp. 25- 29 ,(2004) , 10.1016/J.SCRIPTAMAT.2004.03.026
H. M. Hindam, W. W. Smeltzer, Application of auger electron spectroscopy and inert metal marker techniques to determine metal and oxygen transport in oxide films on metals Oxidation of Metals. ,vol. 14, pp. 337- 349 ,(1980) , 10.1007/BF00603789
AGEA Rabiei, AG Evans, Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings Acta Materialia. ,vol. 48, pp. 3963- 3976 ,(2000) , 10.1016/S1359-6454(00)00171-3
H. Echsler, V. Shemet, M. Schütze, L. Singheiser, W. J. Quadakkers, Cracking in and around the thermally grown oxide in thermal barrier coatings: A comparison of isothermal and cyclic oxidation Journal of Materials Science. ,vol. 41, pp. 1047- 1058 ,(2006) , 10.1007/S10853-005-3639-3