Process Optimization and Properties of Laser Cladding High Vanadium High Speed Steel Coatings on Nodular Cast Iron
作者： Ni Jun Xu , Jian Bin Lv , Ting Sun , Chang Sheng Liu
DOI: 10.4028/WWW.SCIENTIFIC.NET/AMR.712-715.611
关键词:
摘要: … 5(c)). The average microhardness at the clad surface was about 650 HV. The reason for that the microhardness of the HAZ is much higher than the substrate is the graphite had diffused …
sci-hub.se 参考文章(5)
Alejandro Sanz, New coatings for continuous casting rolls Surface & Coatings Technology. ,vol. 177, pp. 1- 11 ,(2003) , 10.1016/J.SURFCOAT.2003.06.024
Yukio Fujii, Kikuo Maeda, Flaking failure in rolling contact fatigue caused by indentations on mating surface (I): Reproduction of flaking failure accompanied by cracks extending bi-directionally relative to the load-movement Wear. ,vol. 252, pp. 787- 798 ,(2002) , 10.1016/S0043-1648(02)00033-9
Ying Ping Ji, Su Jun Wu, Liu Jie Xu, Yan Li, Shi Zhong Wei, Effect of carbon contents on dry sliding wear behavior of high vanadium high speed steel Wear. ,vol. 294, pp. 239- 245 ,(2012) , 10.1016/J.WEAR.2012.07.003
Shizhong Wei, Jinhua Zhu, Leujue Xu, Research on wear resistance of high speed steel with high vanadium content Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 404, pp. 138- 145 ,(2005) , 10.1016/J.MSEA.2005.05.062
Shizhong Wei, Zhu Jinhua, Xu Liujie, Long Rui, Effects of carbon on microstructures and properties of high vanadium high-speed steel Materials & Design. ,vol. 27, pp. 58- 63 ,(2006) , 10.1016/J.MATDES.2004.09.027