Effect of Hydration Products Transformation for Compressive Strength of Autoclaved Silicate Products
作者： Chang Jun Ke , Shu Ying Wang , Jun Li Liu
DOI: 10.4028/WWW.SCIENTIFIC.NET/AMM.204-208.3644
关键词:
摘要: the relationship between hydration products transformation and compressive strength was studied with X-ray diffraction, infrared spectroscopy analysis. The results showed, 0.505nm hydrogarnets diffraction peaks weakened 0.183nm CSH peak enhanced different autoclaved time under 1.2MPa saturated steam pressure. lower pressure for autoclaving 6h, then weaken higher And 6h. During autoclaving, hydrogarnet translate into Al-substituted calcium silicate hydrate (C-S-H). Transformation of is favorable sample.
harvard.edu
sci-hub.se 参考文章(2)
Danielle S Klimesch, Abhi Ray, DTA-TGA evaluations of the CaO–Al2O3–SiO2–H2O system treated hydrothermally Thermochimica Acta. ,vol. 334, pp. 115- 122 ,(1999) , 10.1016/S0040-6031(99)00140-9
D. S. Klimesch, A. S. Ray, Effect of quartz content on the nature of Al-substituted 11 Å tobermorite in hydrothermally treated CaO-Al2O3-SiO2-H2O systems Advances in Cement Research. ,vol. 11, pp. 179- 187 ,(1999) , 10.1680/ADCR.1999.11.4.179