Mechanism of fatigue failure in ultralong life regime
作者： Y. MURAKAMI , N. N. YOKOYAMA , J. NAGATA
DOI: 10.1046/J.1460-2695.2002.00576.X
关键词:
摘要: … Fatigue strength of high strength steels is sensitive to small defects and to inclusions. If we imagine the many possible factors which may influence fatigue strength during such a long …
sci-hub.se 参考文章(16)
W.R Heller, Quantum effects in diffusion: Internal friction due to hydrogen and deuterium dissolved in α-iron Acta Metallurgica. ,vol. 9, pp. 600- 613 ,(1961) , 10.1016/0001-6160(61)90165-1
Y. Murakami, T. Nomoto, T. Ueda, Y. Murakami, On the mechanism of fatigue failure in the superlong life regime (N>107 cycles). Part 1: influence of hydrogen trapped by inclusions Fatigue & Fracture of Engineering Materials & Structures. ,vol. 23, pp. 893- 902 ,(2000) , 10.1046/J.1460-2695.2000.00328.X
T. Tabata, H.K. Birnbaum, Direct observations of the effect of hydrogen on the behavior of dislocations in iron Scripta Metallurgica. ,vol. 17, pp. 947- 950 ,(1983) , 10.1016/0036-9748(83)90268-5
Y MURAKAMI, M ENDO, Effects of defects, inclusions and inhomogeneities on fatigue strength International Journal of Fatigue. ,vol. 16, pp. 163- 182 ,(1994) , 10.1016/0142-1123(94)90001-9
H. Matsui, H. Kimura, S. Moriya, The effect of hydrogen on the mechanical properties of high purity iron I. Softening and hardening of high purity iron by hydrogen charging during tensile deformation Materials Science and Engineering. ,vol. 40, pp. 207- 216 ,(1979) , 10.1016/0025-5416(79)90191-5
James A. Clum, The role of hydrogen in dislocation generation in iron alloys Scripta Metallurgica. ,vol. 9, pp. 51- 58 ,(1975) , 10.1016/0036-9748(75)90145-3
DR Petersen, Y Murakami, T Toriyama, EM Coudert, Instructions for a New Method of Inclusion Rating and Correlations with the Fatigue Limit Journal of Testing and Evaluation. ,vol. 22, pp. 318- 326 ,(1994) , 10.1520/JTE11840J
Takeshi Naito, Hideo Ueda, Masao Kikuchi, Fatigue behavior of carburized steel with internal oxides and nonmartensitic microstructure near the surface Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 15, pp. 1431- 1436 ,(1984) , 10.1007/BF02648572
Miller, O’donnell, The fatigue limit and its elimination Fatigue & Fracture of Engineering Materials & Structures. ,vol. 22, pp. 545- 557 ,(1999) , 10.1046/J.1460-2695.1999.00204.X
Y Murakam, T Nomoto, T Ueda, Factors influencing the mechanism of superlong fatigue failure in steels Fatigue & Fracture of Engineering Materials & Structures. ,vol. 22, pp. 581- 590 ,(1999) , 10.1046/J.1460-2695.1999.00187.X