Fracture toughness variation induced by stress corrosion cracking of prestressing steels
作者： J. Sanchez , J. Fullea , C. Andrade
关键词:
摘要: The authors wish to thank Ministerio de Fomento of Spain for the funding accomplishment project Non-destructive methods and strategies control corrosion in pretested steels, INGENIO 2010-CONSOLIDER on Safety durability structures: SEDUREC and, specially, Professor Gustavo Guinea (UPM).
core.ac.uk
sci-hub.se 参考文章(7)
J. Sanchez, J. Fullea, C. Andrade, C. Alonso, Stress corrosion cracking mechanism of prestressing steels in bicarbonate solutions Corrosion Science. ,vol. 49, pp. 4069- 4080 ,(2007) , 10.1016/J.CORSCI.2007.05.025
J. Toribio, Relationship between microstructure and strength in eutectoid steels Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 387, pp. 227- 230 ,(2004) , 10.1016/J.MSEA.2004.01.084
J Toribio, V Kharin, Localized plasticity near a crack tip in a strain hardening material subjected to mode I loading Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 319, pp. 535- 539 ,(2001) , 10.1016/S0921-5093(01)01029-2
A. Levan, J. Royer, Part-circular surface cracks in round bars under tension, bending and twisting International Journal of Fracture. ,vol. 61, pp. 71- 99 ,(1993) , 10.1007/BF00032340
A. Valiente, M. Elices, Premature failure of prestressed steel bars Engineering Failure Analysis. ,vol. 5, pp. 219- 227 ,(1998) , 10.1016/S1350-6307(98)00002-8
J. R. Rice, A Path Independent Integral and the Approximate Analysis of Strain Concentration by Notches and Cracks Journal of Applied Mechanics. ,vol. 35, pp. 379- 386 ,(1968) , 10.1115/1.3601206
G R Irwin, ANALYSIS OF STRESS AND STRAINS NEAR THE END OF A CRACK TRAVERSING A PLATE Journal of Applied Mechanics. ,vol. 24, pp. 0- 0 ,(1957)