Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steel in Pure Water
作者： Xing-Chen Liu , Hong-Liang Ming , Zhi-Ming Zhang , Jian-Qiu Wang , Li-Chen Tang
DOI: 10.1007/S40195-019-00929-9
关键词:
摘要: In pressurized water reactor, fretting corrosion has become the main reason for failure of 690TT heat exchanger tubes. The effect temperature on behavior between tube and 405 stainless steel (SS) bar been studied during 106 cycles. overall average coefficient friction (COF) values descends with an increase in test temperature, while width worn scar becomes wider. severest happens when is at 100 °C. wear mechanism differs different temperatures, from adhesive room to abrasive delamination 100 °C, 200 °C. Deformation slips, high residual strain concentration, micro-cracks are found which disadvantageous further service performance
springer.com
sci-hub.se 参考文章(32)
Z.H. Wang, Y.H. Lu, J. Li, T. Shoji, Effect of pH value on the fretting wear behavior of Inconel 690 alloy Tribology International. ,vol. 95, pp. 162- 169 ,(2016) , 10.1016/J.TRIBOINT.2015.10.025
Zhiming Zhang, Jianqiu Wang, En-Hou Han, Wei Ke, Influence of dissolved oxygen on oxide films of Alloy 690TT with different surface status in simulated primary water Corrosion Science. ,vol. 53, pp. 3623- 3635 ,(2011) , 10.1016/J.CORSCI.2011.07.012
Wenjun Kuang, Xinqiang Wu, En-Hou Han, Influence of dissolved oxygen concentration on the oxide film formed on 304 stainless steel in high temperature water Corrosion Science. ,vol. 63, pp. 259- 266 ,(2012) , 10.1016/J.CORSCI.2012.06.007
Jae Yong Yun, Myung Chul Park, Gyeong Su Shin, Ji Haeng Heo, Dae Il Kim, Seon Jin Kim, Effects of amplitude and frequency on the wear mode change of Inconel 690 SG tube mated with SUS 409 Wear. ,vol. 313, pp. 83- 88 ,(2014) , 10.1016/J.WEAR.2014.02.019
F. Huang, J.Q. Wang, E.H. Han, W. Ke, Short-time Oxidation of Alloy 690 in High-temperature and High-pressure Steam and Water Journal of Materials Science & Technology. ,vol. 28, pp. 562- 568 ,(2012) , 10.1016/S1005-0302(12)60098-X
Hua Sun, Xinqiang Wu, En-Hou Han, Effects of temperature on the oxide film properties of 304 stainless steel in high temperature lithium borate buffer solution Corrosion Science. ,vol. 51, pp. 2840- 2847 ,(2009) , 10.1016/J.CORSCI.2009.08.006
Seung Mo Hong, In Sup Kim, Impact fretting wear of alloy 690 tubes at 25 °C and 290 °C Wear. ,vol. 259, pp. 356- 360 ,(2005) , 10.1016/J.WEAR.2005.02.020
M. Helmi Attia, Fretting fatigue and wear damage of structural components in nuclear power stations—Fitness for service and life management perspective Tribology International. ,vol. 39, pp. 1294- 1304 ,(2006) , 10.1016/J.TRIBOINT.2006.02.052
Wenjun Kuang, Xinqiang Wu, En-Hou Han, Jiancun Rao, The mechanism of oxide film formation on Alloy 690 in oxygenated high temperature water Corrosion Science. ,vol. 53, pp. 3853- 3860 ,(2011) , 10.1016/J.CORSCI.2011.07.038
J. Li, Y.H. Lu, Effects of displacement amplitude on fretting wear behaviors and mechanism of Inconel 600 alloy Wear. ,vol. 304, pp. 223- 230 ,(2013) , 10.1016/J.WEAR.2013.04.027