An Assessment of the Interlaminar Stress Problem in Laminated Composites
作者： Nicholas J. Salamon
DOI: 10.1177/002199838001400114
关键词:
摘要: A review and assessment of the interlaminar delamination problem com mon to layered composite materials is presented. The work covers calcula tion stresses from a homogeneous microstructural material viewpoint as well background information on singularity problem. observation edge experimental efforts are discussed together with recent fracture mechanics studies. conclu sions provides an suggestions for future investigation.
sagepub.com
sci-hub.se 参考文章(59)
RB Pipes, BE Kaminski, NJ Pagano, Influence of the free edge upon the strength of angle-ply laminates ASTM special technical publications. pp. 218- 228 ,(1973) , 10.1520/STP36487S
C. T. Herakovich, A. Nagarkar, D. A. Obrien, Failure analysis of composite laminates with free edges ,(1979)
JM. Whitney, Free-Edge Effects in the Characterization of Composite Materials ASTM special technical publications. pp. 167- 180 ,(1973) , 10.1520/STP36484S
Giuseppe Grioli, Mathematical Theory of Elastic Equilibrium: Recent Results ,(1962)
Nicholas J. Salamon, A finite-difference program for stresses in anisotropic, layered plates in bending ,(1975)
R. Byron Pipes, N.J. Pagano, Interlaminar Stresses in Composite Laminates Under Uniform Axial Extension Journal of Composite Materials. ,vol. 4, pp. 538- 548 ,(1970) , 10.1177/002199837000400409
N. J. PAGANO, L. M. LACKMAN, Prevention of Delamination of Composite Laminates AIAA Journal. ,vol. 13, pp. 399- 401 ,(1975) , 10.2514/3.49713
NJ. Salamon, Stress Distribution in Sandwich Beams in Uniform Bending ASTM special technical publications. pp. 166- 177 ,(1981) , 10.1520/STP29309S
Milton S. Hess, The End Problem for a Laminated Elastic Strip — II. Differential Expansion Stresses Journal of Composite Materials. ,vol. 3, pp. 630- 641 ,(1969) , 10.1177/002199836900300404
Alexander Harris, Oscar Orringer, Investigation of Angle-Ply Delamination Specimen For Interlaminar Strength Test Journal of Composite Materials. ,vol. 12, pp. 285- 299 ,(1978) , 10.1177/002199837801200306