Hydrogen embrittlement during the corrosion of steel by wet elemental sulphur
作者： R. Gee , Z.Y. Chen
DOI: 10.1016/0010-938X(95)00088-2
关键词:
摘要: … atoms into the lattice of the metal that causes embrittlement and, as a result, possible … can provide the hydrogen source for embrittlement. A rupture of a high pressure transport line for …
elsevier.com
sci-hub.se 参考文章(19)
Beat Meyer, Sulfur, Energy, and Environment ,(2013)
J. M. West, Basic corrosion and oxidation ,(1980)
H. Fischer, U.H.F. Sander, R. Kola, U. Rothe, Sulphur, sulphur dioxide and sulphuric acid. Sulphur, sulphur dioxide and sulphuric acid.. ,(1984)
J. R. Postgate, The sulphate-reducing bacteria ,(1979)
J.C. Scully, THE THEORY OF STRESS CORROSION CRACKING IN ALLOYS Anti-Corrosion Methods and Materials. ,vol. 19, pp. 5- 10 ,(1972) , 10.1108/EB006879
Günter Schmitt, Ludger Sobbe, Wolfgang Bruckhoff, Corrosion and hydrogen-induced cracking of pipeline steel in moist triethylene glycol diluted with liquid hydrogen sulfide Corrosion Science. ,vol. 27, pp. 1071- 1076 ,(1987) , 10.1016/0010-938X(87)90099-0
W. J. Tomlinson, D. M. Meades, Technical Note: Elemental Sulfur and the Corrosion and Cracking of Type 304 Stainless Steel Corrosion. ,vol. 47, pp. 269- 271 ,(1991) , 10.5006/1.3585254
Digby D. MacDonald, Bruce Roberts, James B. Hyne, The corrosion of carbon steel by wet elemental sulphur Corrosion Science. ,vol. 18, pp. 411- 425 ,(1978) , 10.1016/S0010-938X(78)80037-7
J. C. Scully, The Fundamentals of Corrosion ,(1966)
Donald P. Smith, Henry Eyring, Hydrogen in metals ,(1948)