Preparation of zirconia sintered body
作者： Yutaka Kimura , Masamichi Obitsu , Makoto Yoshinari
DOI:
关键词:
摘要: Zirconia sintered bodies are produced by injection molding a zirconia composition comprising powder and an organic binder firing the molded composition. High density having strength, white transparency smoothness obtained when containing 2 to 10 mol % of yttria in solid solution form specific surface area up 12 m2 /g as measured BET method product average particle size 3 μm·m2 is used.
lens.org 参考文章(7)
Etsuro Kato, Powder of coagulated spherical zirconia particles and process for producing them ,(1986)
Shingo Sasaki, Tadaaki Matsuhisa, Process for dewaxing ceramic molded bodies ,(1985)
Isao Nissan Chemical Industries Ltd. Tomi, O Nissan Chemical Industries Ltd. Kaga, Masamichi Nissan Chemical Industries Ltd. Obitsu, Takao C, Process for manufacturing fine zirconium oxide powder ,(1987)
Doris Peuckert, Gangolf Kriechbaum, Peter Kleinschmit, Zirconium oxide powder ,(1988)
Robert Dean Silvers, Anthony Joseph Fanelli, Aqueous compositions for injection moulding comprising a gel-forming material and ceramic and/or metal powder ,(1987)
Takao Kaga, Masamichi Kohitsu, Isao Tomi, Production of zirconium oxide fine powder ,(1987)
Kato Etsuro, POWDER OF ZIRCONIA AGGLOMERATED PARTICLE AND PREPARATION THEREOF ,(1986)