Susceptibility to Stress Corrosion Cracking of 254SMO SS
作者： Lorenzo De Micheli , Silvia Maria Leite Agostinho , Giordano Trabanelli , Fabrizio Zucchi
DOI: 10.1590/S1516-14392002000100011
关键词:
摘要: Received: April 25, 2001; Revised: October 18, 2001The susceptibility to stress corrosion cracking (SCC) of solubilized and sensitized 254SMO SSwas studied in sodium chloride, fluoride solutions at 80 °C sulfuric acid solutionsin presence chloride 25 °C. The influence salt concentration, pH values theaddition thiosulfate was examined. SCC evaluated by Slow Strain RateTests (SSRT), 1.5 x 10
fapesp.br
sci-hub.st 参考文章(8)
L. de Micheli, C.A. Barbosa, A.H.P. Andrade, S.M.L. Agostinho, Electrochemical behaviour of 254SMO stainless steel in comparison with 316L stainless steel and Hastelloy C276 in HCl media British Corrosion Journal. ,vol. 35, pp. 297- 300 ,(2000) , 10.1179/000705900101501371
F Zucchi, G Trabanelli, G Demertzis, The intergranular stress corrosion cracking of a sensitized AISI 304 IN NaF and NaCl solutions Corrosion Science. ,vol. 28, pp. 69- 79 ,(1988) , 10.1016/0010-938X(88)90008-X
R.C. Newman, T. Shahrabi, The effect of alloyed nitrogen or dissolved nitrate ions on the anodic behaviour of austenitic stainless steel in hydrochloric acid Corrosion Science. ,vol. 27, pp. 827- 838 ,(1987) , 10.1016/0010-938X(87)90040-0
Jan Olsson, Horst Grützner, Experiences with a high‐alloyed stainless steel under highly corrosive conditions Materials and Corrosion-werkstoffe Und Korrosion. ,vol. 40, pp. 279- 284 ,(1989) , 10.1002/MACO.19890400504
D.B. Wells, J. Stewart, R. Davidson, P.M. Scott, D.E. Williams, The mechanism of intergranular stress corrosion cracking of sensitised austenitic stainless steel in dilute thiosulphate solution Corrosion Science. ,vol. 33, pp. 39- 71 ,(1992) , 10.1016/0010-938X(92)90017-W
H. P. Leckie, H. H. Uhlig, Environmental Factors Affecting the Critical Potential for Pitting in 18–8 Stainless Steel Journal of The Electrochemical Society. ,vol. 113, pp. 1262- 1267 ,(1966) , 10.1149/1.2423801
E. A. Ashour, E. A. Abd El Meguid, B. G. Ateya, Effects of Thiosulfate on Susceptibility of Type 316 Stainless Steel to Stress Corrosion Cracking in 3.5% Aqueous Sodium Chloride Corrosion. ,vol. 53, pp. 612- 616 ,(1997) , 10.5006/1.3290293
R. Nishimura, SCC Failure Prediction of Austenitic Stainless Steels in Acid Solutions—Effect of pH, Anion Species, and Concentration CORROSION. ,vol. 46, pp. 311- 318 ,(1990) , 10.5006/1.3585109