Na 2 O-B 2 O 3 -SiO 2 玻璃焊料连接碳化硅陶瓷接口抗热震性能
作者： 罗朝华, 江东亮, 张景贤, 林庆玲, 陈忠明, 黄政仁
DOI: 10.3724/SP.J.1077.2012.00234
关键词:
摘要: 采用水淬法对以Na 2 O-B O 3 -SiO 体系玻璃焊料连接的常压烧结碳化硅试条的抗热震性能进行了研究. 对不同温度下淬火后接口以及断面处微观结构进行了比较与分析, 并对比了不同淬火温度以及固定淬火温度为150℃时多次热循环后连接试条的残余弯曲强度. 结果表明, 对于单次淬火, 当淬火温度为150℃时, 由于热应力引起中间层内部微裂纹扩展, 导致残余弯曲强度迅速降低到(152±28) MPa. 淬火温度在150℃~320℃时, 中间层内部裂纹保持在亚临界状态, 相应弯曲强度基本保持在140 继续升高淬火温度至420℃时, 裂纹进一步扩展, 试条残余弯曲强度迅速降低至(32±8) 对于多次热循环, 当淬火温度固定在150℃时, 经多次热循环, 残余弯曲强度与热循环次数变化不明显, 基本保持在120 MPa左右, 这说明在150℃以下淬火, 连接试条具有较好的抗热循环冲击性能.
jim.org.cn参考文章(11)
Zhihong Zhong, Tatsuya Hinoki, Akira Kohyama, Joining of Silicon Carbide to Ferritic Stainless Steel Using a W–Pd–Ni Interlayer for High‐Temperature Applications International Journal of Applied Ceramic Technology. ,vol. 7, pp. 338- 347 ,(2009) , 10.1111/J.1744-7402.2009.02461.X
G.J Qiao, C.G Zhang, Z.H Jin, Thermal cyclic test of alumina/kovar joint brazed by Ni–Ti active filler Ceramics International. ,vol. 29, pp. 7- 11 ,(2003) , 10.1016/S0272-8842(02)00081-0
Toshihiro Yamada, Motohiro Satoh, Akiomi Kohno, Kazuaki Yokoi, Residual stress estimation of a silicon carbide-Kovar joint Journal of Materials Science. ,vol. 26, pp. 2887- 2892 ,(1991) , 10.1007/BF01124817
M. Dimitrijevic, M. Posarac, J. Majstorovic, T. Volkov-Husovic, B. Matovic, Behavior of silicon carbide/cordierite composite material after cyclic thermal shock Ceramics International. ,vol. 35, pp. 1077- 1081 ,(2009) , 10.1016/J.CERAMINT.2008.04.029
Timothy J. Perham, Lutgard C. Jonghe, Warren J. MoberlyChan, Joining of Silicon Carbide with a Cordierite Glass-Ceramic Journal of the American Ceramic Society. ,vol. 82, pp. 297- 305 ,(2004) , 10.1111/J.1551-2916.1999.TB20061.X
P Colombo, B Riccardi, A Donato, G Scarinci, Joining of SiC/SiCf ceramic matrix composites for fusion reactor blanket applications Journal of Nuclear Materials. ,vol. 278, pp. 127- 135 ,(2000) , 10.1016/S0022-3115(99)00268-8
A. Makishima, J.D. Mackenzie, Direct calculation of Young's moidulus of glass Journal of Non-crystalline Solids. ,vol. 12, pp. 35- 45 ,(1973) , 10.1016/0022-3093(73)90053-7
Akio Makishima, John D. Mackenzie, Calculation of bulk modulus, shear modulus and Poisson's ratio of glass Journal of Non-Crystalline Solids. ,vol. 17, pp. 147- 157 ,(1975) , 10.1016/0022-3093(75)90047-2
Zhu Dingyi, Ma Mingliang, Jin Zhihao, Wang Yonglan, The effect of molybdenum net interlayer on thermal shock resistance of Al2O3/Nb brazed joint Journal of Materials Processing Technology. ,vol. 96, pp. 19- 21 ,(1999) , 10.1016/S0924-0136(99)00078-3
M. Singh, A reaction forming method for joining of silicon carbide-based ceramics Scripta Materialia. ,vol. 37, pp. 1151- 1154 ,(1997) , 10.1016/S1359-6462(97)00233-9