Analysis of internal cracks in high carbon casting bloom induced by soft reduction process and its improvement using numerical simulations and industrial experiments
作者： Nanfu Zong , Jian Huang , Jun Liu , Sida Ma , Tao Jing
关键词:
摘要: … industrial practices, however, internal cracks are always observed between the surface … soft reduction technologies [2–7]. Internal cracks induced in as-cast blooms by the soft reduction …
sci-hub.st 参考文章(14)
Cheng Ji, Sen Luo, Miaoyong Zhu, Analysis and Application of Soft Reduction Amount for Bloom Continuous Casting Process Isij International. ,vol. 54, pp. 504- 510 ,(2014) , 10.2355/ISIJINTERNATIONAL.54.504
S. Luo, M. Zhu, C. Ji, Theoretical model for determining optimum soft reduction zone of continuous casting steel Ironmaking & Steelmaking. ,vol. 41, pp. 233- 240 ,(2014) , 10.1179/1743281213Y.0000000126
Wenjun Wang, Linxin Ning, Raimund Bülte, Wolfgang Bleck, Formation of internal cracks in steel billets during soft reduction Journal of University of Science and Technology Beijing, Mineral, Metallurgy, Material. ,vol. 15, pp. 114- 119 ,(2008) , 10.1016/S1005-8850(08)60023-7
Xiao-bin Li, Hua Ding, Zheng-you Tang, Ji-cheng He, Formation of internal cracks during soft reduction in rectangular bloom continuous casting International Journal of Minerals Metallurgy and Materials. ,vol. 19, pp. 21- 29 ,(2012) , 10.1007/S12613-012-0510-9
H.K.D.H. Bhadeshia, Steels for bearings Progress in Materials Science. ,vol. 57, pp. 268- 435 ,(2012) , 10.1016/J.PMATSCI.2011.06.002
Young Mok Won, Tae-Jung Yeo, Dong Jin Seol, Kyu Hwan Oh, A new criterion for internal crack formation in continuously cast steels Metallurgical and Materials Transactions B-process Metallurgy and Materials Processing Science. ,vol. 31, pp. 779- 794 ,(2000) , 10.1007/S11663-000-0115-Y
D. N. Lee, H. N. Han, K. H. Oh, Y. Lee, T. Yeo, K. Kim, Analysis of surface and internal cracks in continuously cast beam blank Ironmaking & Steelmaking. ,vol. 24, pp. 249- 256 ,(1997)
Hanghang An, Yan Ping Bao, Min Wang, Li Hua Zhao, Reducing macro segregation of high carbon steel in continuous casting bloom by final electromagnetic stirring and mechanical soft reduction integrated process Metallurgical Research & Technology. ,vol. 114, pp. 405- ,(2017) , 10.1051/METAL/2017029
Nanfu Zong, Yang Liu, Hui Zhang, Application of chamfered narrow face mold technology to reduce longitudinal surface crack defects of hyperperitectic steel generated during flexible thin slab casting process Metallurgical Research & Technology. ,vol. 114, pp. 413- ,(2017) , 10.1051/METAL/2017030
Nanfu Zong, Hui Zhang, Yang Liu, Zhifang Lu, Analysis on morphology and stress concentration in continuous casting bloom to learn the formation and propagation of internal cracks induced by soft reduction technology Ironmaking & Steelmaking. ,vol. 46, pp. 872- 885 ,(2019) , 10.1080/03019233.2018.1556911