Exchange of experience the effect of synthesis time on the wear behavior of Al–8%Ti alloy produced by mechanical alloying
作者： D. Özyürek , S. Tekeli , T. Tuncay , R. Yilmaz
DOI: 10.1007/S11106-012-9459-5
关键词:
摘要: In this study, Al–8%Ti alloy was produced by mechanical alloying. The powders were cold pressed at 630 MPa and synthesized 600°C for 12 24 h under argon gas atmosphere. After synthesis processes, the specimens examined SEM, XRD, hardness tests. Wear tests carried out dry sliding conditions using a pin-on-disk type machine constant load of 30 N speed 1 m/sec. Total distances selected as 500, 1000, 1500, 2000 m. experimental results showed that density Al–%8Ti increased with increasing time. It also observed volume reduction distance decreased
springer.com
sci-hub.se 参考文章(11)
I.C Barlow, H Jones, W.M Rainforth, The effect of heat treatment at 500–655 °C on the microstructure and properties of mechanically alloyed Al–Ti–O based material Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 351, pp. 344- 357 ,(2003) , 10.1016/S0921-5093(02)00860-2
L.J Yang, Wear coefficient equation for aluminium-based matrix composites against steel disc Wear. ,vol. 255, pp. 579- 592 ,(2003) , 10.1016/S0043-1648(03)00191-1
D. Roy, S.S. Singh, B. Basu, W. Lojkowski, R. Mitra, I. Manna, Studies on wear behavior of nano-intermetallic reinforced Al-base amorphous/nanocrystalline matrix in situ composite Wear. ,vol. 266, pp. 1113- 1118 ,(2009) , 10.1016/J.WEAR.2009.03.015
A. Mandal, B.S. Murty, M. Chakraborty, Sliding wear behaviour of T6 treated A356–TiB2 in-situ composites Wear. ,vol. 266, pp. 865- 872 ,(2009) , 10.1016/J.WEAR.2008.12.011
Sanjay Kumar Thakur, Manoj Gupta, Improving mechanical performance of Al by using Ti as reinforcement Composites Part A-applied Science and Manufacturing. ,vol. 38, pp. 1010- 1018 ,(2007) , 10.1016/J.COMPOSITESA.2006.06.014
Tiezheng Li, Fengchun Jiang, Eugene A. Olevsky, Kenneth S. Vecchio, Marc A. Meyers, Damage evolution in Ti6Al4V–Al3Ti metal-intermetallic laminate composites Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 443, pp. 1- 15 ,(2007) , 10.1016/J.MSEA.2006.05.037
Debdas Roy, Bikramjit Basu, Amitava Basu Mallick, Tribological properties of Ti-aluminide reinforced Al-based in situ metal matrix composite Intermetallics. ,vol. 13, pp. 733- 740 ,(2005) , 10.1016/J.INTERMET.2004.11.005
Xiaoming Wang, Animesh Jha, Rik Brydson, In situ fabrication of Al3Ti particle reinforced aluminium alloy metal–matrix composites Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 364, pp. 339- 345 ,(2004) , 10.1016/J.MSEA.2003.08.049
A.P. Sannino, H.J. Rack, Dry sliding wear of discontinuously reinforced aluminum composites: review and discussion Wear. ,vol. 189, pp. 1- 19 ,(1995) , 10.1016/0043-1648(95)06657-8
V. Abbasi Chianeh, H.R. Madaah Hosseini, M. Nofar, Micro structural features and mechanical properties of Al-Al3Ti composite fabricated by in-situ powder metallurgy route Journal of Alloys and Compounds. ,vol. 473, pp. 127- 132 ,(2009) , 10.1016/J.JALLCOM.2008.05.068