Temperature effects on mixed mode I/II delamination under quasi-static and fatigue loading of a carbon/epoxy composite
作者： Georgia Charalambous , Giuliano Allegri , Stephen R. Hallett
DOI: 10.1016/J.COMPOSITESA.2015.05.016
关键词:
摘要: … on the mixed-mode interlaminar fracture toughness and fatigue delamination growth rate of a … behaviour of the carbon-epoxy composite at variable temperatures has been made in …
core.ac.uk
imperial.ac.uk
bristol.ac.uk
sci-hub.se 参考文章(35)
W. L. Bradley, D. H. Allen, J. R. Reeder, Effect of Elevated Temperature and Loading Rate on Delamination Fracture Toughness ,(2003)
Emily J. Biss, Alan T. Nettles, Low Temperature Mechanical Testing of Carbon-Fiber/Epoxy-Resin Composite Materials ,(1996)
William M. Johnston, Gregory J. Toland, T. Kevin O'Brien, Mode II Interlaminar Fracture Toughness and Fatigue Characterization of a Graphite Epoxy Composite Material ,(2010)
TK O'Brien, GB Murri, SA Salpekar, Interlaminar shear fracture toughness and fatigue thresholds for composite materials ASTM International. ,(1989) , 10.1520/STP10418S
G. Hartwig, S. Knaak, Fibre-epoxy composites at low temperatures Cryogenics. ,vol. 24, pp. 639- 647 ,(1984) , 10.1016/0011-2275(84)90083-3
J. Wolfrum, S. Eibl, L. Lietch, Rapid evaluation of long-term thermal degradation of carbon fibre epoxy composites Composites Science and Technology. ,vol. 69, pp. 523- 530 ,(2009) , 10.1016/J.COMPSCITECH.2008.11.018
A. J. Kinloch, J. G. Williams, Crack blunting mechanisms in polymers Journal of Materials Science. ,vol. 15, pp. 987- 996 ,(1980) , 10.1007/BF00552112
Dennis A Burianek, S.Mark Spearing, Delamination growth from face sheet seams in cross-ply titanium/graphite hybrid laminates Composites Science and Technology. ,vol. 61, pp. 261- 269 ,(2001) , 10.1016/S0266-3538(00)00206-2
Anders Sjögren, Leif E Asp, Effects of temperature on delamination growth in a carbon/epoxy composite under fatigue loading International Journal of Fatigue. ,vol. 24, pp. 179- 184 ,(2002) , 10.1016/S0142-1123(01)00071-8
Alan J. Russell, Micromechanisms of interlaminar fracture and fatigue Polymer Composites. ,vol. 8, pp. 342- 351 ,(1987) , 10.1002/PC.750080509