Influence of Surface Roughness Skewness on Rolling Contact Fatigue Life
作者： Yoshinobu Akamatsu , Noriyuki Tsushima , Toshihide Goto , Kenji Hibi
DOI: 10.1080/10402009208982180
关键词:
摘要: … of peeling failure. At the surfaces of - 1.38 and - 1.97 Sk rings, there was no peeling failure. However, … probability density function, In order to prolong rolling bearing fatigue life under the …
harvard.edu
sci-hub.se 参考文章(7)
M Tokuda, M Nagafuchi, N Tsushima, H Muro, Observations of the peeling mode of failure and surface-originated flaking from a ring-to-ring rolling contact fatigue test rig ASTM special technical publications. pp. 150- 165 ,(1982) , 10.1520/STP36138S
Nadir Patir, H. S. Cheng, An Average Flow Model for Determining Effects of Three-Dimensional Roughness on Partial Hydrodynamic Lubrication Journal of Lubrication Technology. ,vol. 100, pp. 12- 17 ,(1978) , 10.1115/1.3453103
P. R. Goglia, T. F. Conry, C. Cusano, The Effects of Surface Irregularities on the Elastohydrodynamic Lubrication of Sliding Line Contacts. Part I—Single Irregularities Journal of Tribology-transactions of The Asme. ,vol. 106, pp. 104- 112 ,(1984) , 10.1115/1.3260845
T. E. Tallian, On Competing Failure Modes in Rolling Contact Tribology Transactions. ,vol. 10, pp. 418- 439 ,(1967) , 10.1080/05698196708972201
J. C. Skurka, Elastohydrodynamic Lubrication of Roller Bearings Journal of Lubrication Technology. ,vol. 92, pp. 281- 288 ,(1970) , 10.1115/1.3451388
J. M. de Mul, J. M. Vree, J. C. Kuypers, The influence of certain raceway dent geometries (3-D) on contact stresses and rating fatigue life of rolling bearings Journal of Tribology-transactions of The Asme. ,vol. 109, pp. 452- 461 ,(1987) , 10.1115/1.3261471
Y. Akamatsu, Peeling Damage Due to Rolling Contact Fatigue SAE transactions. ,vol. 98, pp. 1405- 1411 ,(1989) , 10.4271/891909