Enhancing the Adhesion Retention by Controlling the Structure of the Adhesion Interphase Between Rubber Compound and Metal. Part I. Effect of Cobalt Salt
作者： Gyung Soo Jeon
关键词:
摘要: The adhesion between cobalt salt-containing rubber compounds and brass-plated steel cords was studied to understand the role of salt as an promoter. An improvement in shown with low loading range 0.5–1 phr, while a significant decline observed high at 2 phr long aging time 15 days under humidity aging. interphase compound cord using Auger electron spectroscopy (AES) showed stable depth profile by incorporation loading, resulting enhancement retention. For salt, grew excessively, especially ZnO layer formed aging, which resulted reduced adhesion.
sci-hub.se 参考文章(34)
Frédéric Wiame, Bekir Salgin, Jolanta Swiatowska-Mrowiecka, Vincent Maurice, Philippe Marcus, Brass Surface Nanochemistry: The Role of Alloying Cu with Zn Journal of Physical Chemistry C. ,vol. 112, pp. 7540- 7543 ,(2008) , 10.1021/JP801739B
Aparna V Shete, Sudhir B Sawant, Vishwas G Pangarkar, Kinetics of fluid–solid reaction with an insoluble product: zinc borate by the reaction of boric acid and zinc oxide Journal of Chemical Technology & Biotechnology. ,vol. 79, pp. 526- 532 ,(2004) , 10.1002/JCTB.1018
Gyung Soo Jeon, Seung Won Jeong, Adhesion of rubber compounds to nano-copper-coated iron plates as studied by AES depth profiles Journal of Adhesion Science and Technology. ,vol. 18, pp. 925- 942 ,(2004) , 10.1163/156856104840471
Gyung Soo Jeon, Ung Il Kang, Seung Won Jeong, Seok Ju Choi, Seok Ho Kim, Adhesion between rubber compounds and ternary-alloy-coated steel cords. Part II: Effects of sulfur and cobalt salt in rubber compounds Journal of Adhesion Science and Technology. ,vol. 19, pp. 1325- 1348 ,(2005) , 10.1163/156856105774784367
Gyung Soo Jeon, Gon Seo, Promotion effect of a chlorotriazine derivative on the adhesion between rubber compounds and a brass-plated steel cord Journal of Adhesion Science and Technology. ,vol. 15, pp. 689- 701 ,(2001) , 10.1163/156856101750430431
Gyung Soo Jeon, Gon Seo, p-Hydroxy-benzoic acid as an adhesion promoter for rubber compounds to a brass-plated steel cord Journal of Adhesion Science and Technology. ,vol. 15, pp. 483- 498 ,(2001) , 10.1163/156856101300157579
W.S. Fulton, D.E. Sykes, G.C. Smith, SIMS depth profiling of rubber-tyre cord bonding layers prepared using 64Zn depleted ZnO Applied Surface Science. ,vol. 252, pp. 7074- 7077 ,(2006) , 10.1016/J.APSUSC.2006.02.105
T Kosec Mikić, I Milošev, B Pihlar, None, Passivity and Corrosion of Cu–xZn (x = 10–40 wt%) Alloys in Borate Buffer Containing Chloride Ions Journal of Applied Electrochemistry. ,vol. 35, pp. 975- 984 ,(2005) , 10.1007/S10800-005-6726-X
Arup K. Chandra, Arabinda Biswas, R. Mukhopadhyay, Anil K. Bhowmick, SEM/EDX studies of the influence of a cobalt adhesion promoter on the interface between rubber skim compounds and tire steel cord Journal of Adhesion Science and Technology. ,vol. 10, pp. 431- 460 ,(1996) , 10.1163/156856196X00526
Pankaj Y. Patil, William J. Van Ooij, Mechanism of adhesion degradation of rubber to brass-plated steel cords Journal of Adhesion Science and Technology. ,vol. 18, pp. 1367- 1394 ,(2004) , 10.1163/1568561042323266