Electron Beam Induced Structure Transformation of MoO3 to MoO2 and A New Phase MoO

摘要: The transformation of MoO3 induced by electron beam irradiation was studied energy-loss spectroscopy (EELS) in combination with diffraction and high-resolution transmission microscopy (HRTEM) techniques. routes structure were dependent on the applied current density. In case low density, MoO2 obtained. high MoO a rock-salt is suggested to be final phase. change oxidation states Mo oxides deduced from features near edge (ELNES) O K-edge. Quantitative analysis successfully employed M3-edge K-edge obtain O/Mo ratio reduced phases. mechanisms different behaviors frame radiolysis enhanced diffusion. Elektronenstrahl induzierte Transformation von nach und eine neue MoO-Phase Die Elektronenstrahl im Transmissions-Elektronenmikroskop (TEM) wurde mit Hilfe Elektronen-Energieverlust Spektrometrie Kombination Elektronenbeugung hochauflosender Transmissions-Elektronenmikroskopie untersucht. Der Reduktionspfad hangt dabei der Elektronendosis ab: Im Falle einer kleinen Stromdichte endet die bei MoO2, wohingegen hoher NaCl-Struktur zu enden scheint. Anderungen Oxidationszustand entlang wurden anhand Feinstruktur Nahkantenbereich Sauerstoff K-Ionisationskante Elektronen-Energieverlust-Spektrum abgeleitet. Eine quantitative Analyse Molybdan M3- erlaubte Bestimmung des O/Mo-Verhaltnisses reduzierten Phasen. Schlieslich mogliche Mechanismen fur unterschiedlichen strukturellen Transformationen Rahmen strahlungsinduzierten Diffusion vorgeschlagen.