An x-ray photo-electron spectroscopy study of the passivity of amorphous Fe-Mo alloys
作者： K. Hashimoto , M. Naka , K. Asami , T. Masumoto
DOI: 10.1016/0010-938X(79)90014-3
关键词:
摘要: Abstract The increase in molybdenum content amorphous FeMoPC alloys facilitates the passivation 1 N HCl contrast to crystalline iron base without chromium. An attempt was made clarify effect of through composition surface film analyzed by XPS. passive consists mainly ferric oxy-hydroxide, while a large amount hexavalent species is found formed active region. interpreted as follows: dissolution necessary for proceeding formation leads precipitation on alloy and result, stifled. This fact with aid ions which are already accumulated alloy/solution interface during dissolution.
elsevier.com
sci-hub.se 参考文章(14)
Norio Sato, Go Okamoto, A Mechanism of the Anodic Passivation of Nickel in Acid Solution –Higher Valence Oxide Film Theory– Materials Transactions Jim. ,vol. 2, pp. 113- 119 ,(1961) , 10.2320/MATERTRANS1960.2.113
K. Asami, K. Hashimoto, S. Shimodaira, XPS determination of compositions of alloy surfaces and surface oxides on mechanically polished iron-chromium alloys Corrosion Science. ,vol. 17, pp. 713- 723 ,(1977) , 10.1016/0010-938X(77)90067-1
K. Asami, K. Hashimoto, S. Shimodaira, X-ray photoelectron spectrum of Fe2+ state in iron oxides Corrosion Science. ,vol. 16, pp. 35- 45 ,(1976) , 10.1016/S0010-938X(76)80005-4
K. Asami, K. Hashimoto, The X-ray photo-electron spectra ofseveral oxides of iron and chromium Corrosion Science. ,vol. 17, pp. 559- 570 ,(1977) , 10.1016/S0010-938X(77)80002-4
K. Sugimoto, Y. Sawada, The role of molybdenum additions to austenitic stainless steels in the inhibition of pitting in acid chloride solutions Corrosion Science. ,vol. 17, pp. 425- 445 ,(1977) , 10.1016/0010-938X(77)90032-4
K. Asami, K. Hashimoto, T. Masumoto, S. Shimodaira, ESCA study of the passive film on an extremely corrosion-resistant amorphous iron alloy Corrosion Science. ,vol. 16, pp. 909- 914 ,(1976) , 10.1016/S0010-938X(76)80010-8
K Hashimoto, K Osada, T Masumoto, S Shimodaira, Characteristics of passivity of extremely corrosion-resistant amorphous iron alloys Corrosion Science. ,vol. 16, pp. 71- 76 ,(1976) , 10.1016/0010-938X(76)90031-7
K. Hashimoto, K. Asami, K. Teramoto, An X-ray photo-electron spectroscopic study on the role of molybdenum in increasing the corrosion resistance of ferritic stainless steels in HC1 Corrosion Science. ,vol. 19, pp. 3- 14 ,(1979) , 10.1016/0010-938X(79)90003-9
K. Asami, K. Hashimoto, S. Shimodaira, An ESCA study of the Fe2+/Fe3+ ratio in passive films on iron-chromium alloys Corrosion Science. ,vol. 16, pp. 387- 391 ,(1976) , 10.1016/0010-938X(76)90125-6
K.S. Kim, W.E. Baitinger, J.W. Amy, N. Winograd, ESCA studies of metal-oxygen surfaces using argon and oxygen ion-bombardment Journal of Electron Spectroscopy and Related Phenomena. ,vol. 5, pp. 351- 367 ,(1974) , 10.1016/0368-2048(74)85023-1