Micromechanisms of fatigue crack growth retardation following overloads
作者： S. Suresh
DOI: 10.1016/0013-7944(83)90051-6
关键词:
摘要: New mechanistic interpretations to rationalize fatigue crack growth retardation due to load excursions are presented. It is reasoned that crack closure arising from residual tensile …
elsevier.com
sci-hub.se 参考文章(35)
B.A. Bilby, G.E. Cardew, I.C. Howard, STRESS INTENSITY FACTORS AT THE TIPS OF KINKED AND FORKED CRACKS Analysis and Mechanics#R##N#Fourth International Conference on Fracture June 1977 University of Waterloo, Canada. pp. 197- 200 ,(1978) , 10.1016/B978-0-08-022142-7.50039-9
Mechanics of Crack Tip Deformation and Extension by Fatigue ASTM International. ,(1967) , 10.1520/STP47234S
O. E. Wheeler, Spectrum Loading and Crack Growth Journal of Basic Engineering. ,vol. 94, pp. 181- 186 ,(1972) , 10.1115/1.3425362
R. P. Wei, N. E. Fenelli, K. D. Unangst, T. T. Shih, Fatigue Crack Growth Response Following a High-Load Excursion in 2219-T851 Aluminum Alloy Journal of Engineering Materials and Technology-transactions of The Asme. ,vol. 102, pp. 280- 292 ,(1980) , 10.1115/1.3224812
Otakar Jonds, R.P. Wei, An exploratory study of delay in fatigue-crack growth International Journal of Fracture. ,vol. 7, pp. 116- 118 ,(1971) , 10.1007/BF00236491
A. K. Vasudévan, S. Suresh, Influence of corrosion deposits on near-threshold fatigue crack growth behavior in 2xxx and 7xxx series aluminum alloys Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 13, pp. 2271- 2280 ,(1982) , 10.1007/BF02648397
T.T. Shih, R.P. Wei, A study of crack closure in fatigue Engineering Fracture Mechanics. ,vol. 6, pp. 19- 32 ,(1974) , 10.1016/0013-7944(74)90044-7
R. O. Ritchie, S. Suresh, C. M. Moss, Near-Threshold Fatigue Crack Growth in 2 1/4 Cr-1Mo Pressure Vessel Steel in Air and Hydrogen Journal of Engineering Materials and Technology-transactions of The Asme. ,vol. 102, pp. 293- 299 ,(1980) , 10.1115/1.3224813
S. Suresh, G. F. Zamiski, D R. O. Ritchie, Oxide-Induced Crack Closure: An Explanation for Near-Threshold Corrosion Fatigue Crack Growth Behavior Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 12, pp. 1435- 1443 ,(1981) , 10.1007/BF02643688
D. L. DAVIDSON, J. LANKFORD, FATIGUE CRACK TIP PLASTICITY RESULTING FROM LOAD INTERACTIONS IN AN ALUMINUM ALLOY Fatigue & Fracture of Engineering Materials & Structures. ,vol. 1, pp. 439- 446 ,(1979) , 10.1111/J.1460-2695.1979.TB01331.X