Microstructural effects in the fatigue behavior of metals and alloys
作者： N. S. Stoloff , D. J. Duquette
DOI: 10.1080/10408437308245845
关键词:
摘要: Abstract : This review examines the various stages of fatigue damage on basis changes in slip character and dislocation sub-structures resulting from solid solution alloying, thermomechanical treatments or precipitation hardening. Cyclic hardening softening are related to life a wide variety alloy systems, including pure metals, commercial alloys, intermetallic compounds directionally solidified eutectics. The influence behavior variations structure produced by processing (e.g., casting defects, inclusions, surface notches) also considered. Finally, effects temperature aggressive environments crack nucleation propagation metallurgical structure.
sci-hub.se 参考文章(235)
P.J.E. Forsyth, SOME METALLOGRAPHIC OBSERVATIONS ON THE FATIGUE OF METALS J. Inst. Metals. ,(1951)
J. D. Landes, R. P. Wei, Correlation between sustained-load and fatigue crack growth in high-strength steels ,(1969)
H. Abdel-Raouf, A. Plumtree, The influence of deformation rate on the cyclic behavior of pure iron Metallurgical Transactions. ,vol. 2, pp. 1863- 1867 ,(1971) , 10.1007/BF02913417
R. Lagneborg, R. Attermo, The effect of combined low-cycle fatigue and creep on the life of austenitic stainless steels Metallurgical Transactions. ,vol. 2, pp. 1821- 1827 ,(1971) , 10.1007/BF02913411
J.M. Barsom, Corrosion-fatigue crack propagation below Engineering Fracture Mechanics. ,vol. 3, pp. 15- 25 ,(1971) , 10.1016/0013-7944(71)90048-8
R. P. Gamble, J. K. Tien, The room temperature fatigue behavior of nickel-base superalloy crystals at ultrasonic frequency Metallurgical Transactions. ,vol. 2, pp. 1933- 1938 ,(1971) , 10.1007/BF02913426
G. M. Sinclair, An Investigation of the Coaxing Effect in Fatigue of Metals Defense Technical Information Center. ,(1952) , 10.21236/ADA319638
G.R. Leverant, M. Gell, FATIGUE OF NICKEL-BASE SUPERALLOYS. pp 505-23 of Ordered Alloys. Structural Applications and Physical Metallurgy. /Kear, Bernard H. (ed.). Baton Rouge, La. Claitor's Publishing Div. (1970).. ,(1970)
C. Michael Hudson, Herbert F. Hardrath, EFFECTS OF CHANGING STRESS AMPLITUDE ON THE RATE OF FATIGUE-CRACK PROPAGATION IN TWO ALUMINUM ALLOYS ,(1961)
W. A. Wood, M. Ronay, W. H. Reimann, MECHANISM OF FATIGUE DEFORMATION AT ELEVATED TEMPERATURES. ,(1964)