Examination of the α-ω two-phase shock-induced microstructure in zirconium and titanium

摘要: Omega (ω) phase is formed in alpha (α) zirconium during dynamic loading and can be retained in the recovered material. The pathway for the α to ω change (or the reverse transformation) is not well understood. Zirconium was shock-loaded and the resulting two-phase microstructure was examined. Electron backscatter diffraction (EBSD) was used to characterize the orientation relationships and habit planes between phases to understand the pathways between α and ω phases and compare to Molecular Dynamics (MD) simulations. Based on key microstructural features, a significant amount of α phase appears to have originated from the reverse transformation from ω-Zr on unloading. Results of microstructural analysis will be discussed, along with implications toward phase transformation pathways.