Magnetic and electrical transport studies of polycrystalline Sr1− x Bi x Fe12O19 (x= 0, 0.01, and 0.02)

摘要: Bismuth-substituted strontium hexaferrites, Sr 1− x Bi x Fe 12 O 19 for x= 0, 0.01 and 0.02, are studied via powder neutron diffraction (ND), magnetization (M) studies, Mössbauer spectroscopy, and electrical transport. ND results show an indication of increasing Fe 2+ at 12k crystallographic sites (which is supported by Mössbauer results), with increasing Bi in the sample. They also suggest an increase in strain due to Bi substitution for the polyhedral associated with 2a and 2b spin-up and 4f 1 spin-down sites. The M measurements over a wide temperature range (3–823 K), shows irreversibility in zero field cooled (ZFC) and field cooled data right below the Curie temperature, along with the Hopkinson peak in the ZFC data. The temperature dependence of saturated magnetization follows the Bloch relation but that of the coercive field shows unconventional behavior. The coercive field data is fitted using an equation …