Structural characterization of ZnCl2 modified tellurite based glasses

摘要: Glass composition 70 TeO2-(30-x) BaO–x ZnCl2; x= 5, 10, 15, 20 and 25 have been prepared by rapid melt quenching technique under controlled atmospheric conditions. Amorphous nature of the samples was confirmed by x-ray diffractogram. The glass transition temperature (Tg) has been determined using differential scanning calorimetry (DSC) and its value is observed to decrease with increase in ZnCl2 content. The peaks in the Raman and FTIR spectra have been estimated by deconvolutation of the spectra and each of deconvoluted spectra exhibits several peaks. IR and Raman spectra of the present glass system indicate that TeO2 exists as TeO3 trigonal pyramidal (tp), TeO4 trigonal bipyramidal (tbp) and TeO6 polyhedra structural units. With increase in zinc halide content, transformation of some of TeO4 structural units into TeO3 structural units is observed Increase in TeO3 structural units shows that non …