Tensile-and fatigue-properties of low alloy steel JIS-SCM435 and carbon steel JIS-SM490B in 115 MPa hydrogen gas

摘要: Slow strain rate tests using smooth specimens of two types of steels, low alloy steel JIS-SCM435 and carbon steel JIS-SM490B, were carried out in nitrogen gas and hydrogen gas under a pressure of 115 MPa at three different temperatures: 233 K, room temperature and 393 K. In nitrogen gas, these steels exhibited the so-called cup-and-cone fracture at every temperature. On the other hand, in hydrogen gas, in both steels a number of cracks initiated on the specimen surface and coalesced with each other at every temperature, which led to a marked reduction in ductility. Nonetheless, even in hydrogen gas, JIS-SCM435 exhibited a certain reduction of area after the stress-displacement curve reached the tensile strength (TS), whereas JIS-SM490B exhibited little, if any, necking in hydrogen gas. In addition, tension-compression fatigue testing at room temperature revealed that in both steels there was no noticeable …