Glass, glass-ceramic, articles and fabrication process
作者： Marie Comte
DOI:
关键词: Silicate glass 、 Chemical engineering 、 Fabrication 、 Mineralogy 、 Lithium 、 Phase (matter) 、 Solid solution 、 Glass-ceramic 、 Materials science
摘要: The present application discloses: (i) novel glass-ceramic materials containing a solid solution of β-quartz or(and) β-spodumene as main crystalline phase(s); (ii) articles made from said materials; (iii) lithium alumino- silicate glasses, precursors such and (iv) methods for preparing the aforesaid materials. invention relates to use SnO2 (0.15 0.3% by weight) CeO2 and/or MnO2 (0.7 1.5% weight), an agent fining material lass recursor.
lens.org 参考文章(15)
Friedrich Siebers, Wolfgang Schmidbauer, Ioannis Kosmas, Reiner Best, Ulrich Schiffner, Erich Rodek, Otmar Becker, Translucent or opaque colored glass-ceramic article providing a cooking surface and its use ,(2005)
Eva Hoelzel, Thorsten Doehring, Hauke Esemann, Ralf Jedamzik, Method for the forming of glass or glass ceramics ,(2003)
Edward Nashed Boulos, James Victor Jones, Reduction of nickel sulphide stones in glass ,(1996)
Philippe Lehuede, Marie Jacqueline Monique Comte, Ronald Leroy Stewart, β-spodumene glass-ceramic materials and process for making the same ,(2007)
William E. Horsfall, Ronald L. Stewart, Lamp reflector substrate, glass, glass-ceramic materials and process for making the same ,(2004)
Toshitaka Yagi, Naoyuki Goto, Crystallized glass, and method for producing crystallized glass ,(2007)
Marie Jacqueline Monique Comte, Glass-ceramic materials, precursor glass thereof and process for making the same ,(2006)
Friedrich Dr. Siebers, Andreas Sprenger, Gerhard Dr. Lautenschläger, Klaus Schneider, Chemically and thermally pre-stressable lithium aluminosilicate float glass of high temperature resistance ,(2005)
Mikhail D Mikhailov, Sergey K Evstropiev, Monique Comte, Anna V Belykh, Sophie Peschiera, Lionel Beunet, Surface-modified glass-ceramics and their preparation ,(2004)
Friedrich Siebers, Peter Nass, Erich Rodek, Transparent glass ceramics that can be darkened by adding vanadium oxide ,(2000)