Improvement of mechanical properties of cold-rolled commercially pure Ti sheet by high density electropulsing

摘要: Abstract Specimens cut from the cold-rolled commercially pure (CP) Ti sheet were treated by high density electropulsing (the maximum current 7.22 kA/mm 2 , pulse period 110 μs). The deformation behaviors of CP specimens at different states determined uniaxial tensile test. microstructure morphologies observed optical microscopy. results show that induced formation fine equal-axial grains and lamellar microstructures, which leads to strength electropulsed higher than conventional annealed Ti. After electropulsing, yield are increased 100 MPa. And has a good plasticity. experimental demonstrate provides an effective approach enhance retain required ductility.