作者: Daniel Horák , Zdeněk Pelzbauer , František Švec , Jiří Labský , Miroslav Bleha
DOI: 10.1002/APMC.1983.051170110
关键词: Copolymer 、 Reactivity (chemistry) 、 Polymer chemistry 、 Glycidyl methacrylate 、 Polymer 、 Specific surface area 、 Reagent 、 Chemistry 、 Surface reactivity 、 Diluent
摘要: Macroporous copolymers of glycidyl methacrylate and ethylene dimethacrylate were synthesized under equal conditions in the presence different solvents as porogenic agents. The products obtained differ porosity, specific surface area, content oxirane groups, shape. reactivity was measured using three substrates having low, medium, high molecular weight (HCl, 4-amino-2,2,6,6-tetramethylpiperidine-N-oxyl, human serum albumin). fraction reacted amount reagent to which would fill area a monomolecular layer calculated found reach minimum for polymers with best developed porous structure, although all cases it is higher than unity. This shows that reaction proceeds not merely on available new approach description reactions macroporous necessary. Makroporose Copolymere aus Glycidylmethacrylat und Ethylendimethacrylat wurden unter gleichen Bedingungen, aber mit verschiedenen Losungsmitteln als porenbildenden Mitteln hergestellt. Die so synthetisierten Produkte unterscheiden sich der Porositat, spezifischen Oberflache, dem Gehalt an Oxirangruppen Form. Ihre Reaktivitat wurde drei im Molekulargewicht unterschiedlichen Substanzen 4-Amino-2,2,6,6-tetramethylpiperidin-N-oxyl menschliches Serum-Albumin) untersucht. Das Verhaltnis ausreagierten Menge des Substrates zur Menge, die spezifische Oberflache einer monomolekularen Schicht bedecken wurde, berechnet gezeigt, das es kleinsten Werte fur Polymere am besten entwickelten Porenstruktur erreicht. Trotzdem sind allen Fallen hoher eins. Daraus folgt, Reaktion nicht nur auf freien erfolgt deswegen ein neuer Zugang Beurteilung Reaktionen makroporosen notwending ist.