The leaching of phase-separated sodium borosilicate glasses
作者： Akio Makishima , J.D. Mackenzie , J.J. Hammel
DOI: 10.1016/0022-3093(79)90150-9
关键词: Boron 、 Borate glass 、 Sodium 、 Solubility 、 Inorganic chemistry 、 Leaching rate 、 Materials science 、 Soda-lime glass 、 Leaching (metallurgy) 、 Borosilicate glass
摘要: Abstract The leaching of phase-separated sodium borosilicate glass in hot water has been studied. Addition small amounts P 2 O 5 , V MoO 3 or WO to the base was found be effective increasing rate. It confirmed that solubility bulk borate (of composition) is much less than same containing . This explains, at least part, why these added oxides can accelerate rate significantly.
harvard.edu
elsevier.com
sci-hub.se 参考文章(4)
W. HALLER, D. H. BLACKBURN, F. E. WAGSTAFF, R. J. CHARLES, Metastable Immiscibility Surface in the System Na2O‐B2O3‐SiO2* Journal of the American Ceramic Society. ,vol. 53, pp. 34- 39 ,(1970) , 10.1111/J.1151-2916.1970.TB11995.X
Thaddeus P. Kobylinski, Joseph J. Hammel, Harold E. Swift, Porous Silica Beads-A Catalyst Support for Removal of Exhaust Gas Pollutants Industrial & Engineering Chemistry Product Research and Development. ,vol. 14, pp. 147- 150 ,(1975) , 10.1021/I360055A003
Kiyohisa EGUCHI, Kenji TASAKA, Shuji TARUMI, Effect of Composition on the Heat-treatment Time for Phase-Separating Borosilicate Glasses and the Time for Leaching the Separated Glasses Journal of the Ceramic Association, Japan. ,vol. 77, pp. 301- 309 ,(1969) , 10.2109/JCERSJ1950.77.889_301
Masaru SHIMBO, Leach-Out Process of Phase Separated Sodium Borosilicate Glass Journal of the Ceramic Association, Japan. ,vol. 80, pp. 277- 284 ,(1972) , 10.2109/JCERSJ1950.80.923_277