Investigation of the Infrared-Active Lattice Vibration in SrCl2

摘要: SrCl2, single crystals were grown by the Czochralsky method. Their reflectivity at 300 K and transmission 4.2 measured for frequencies from 10 to 930 cm−1 150 cm−1, respectively. The reststrahl band found in reflection spectrum has been analyzed means of a classical oscillator model. In addition, Kramers-Kronig analysis was performed since satisfactory fit could not be achieved with TO-mode LO-mode determined 138 233 A pronounced shoulder on observed as is also case CaF2, BaF2 etc. Its origin discussed terms multi-phonon processes. results measurements show that transparent far infrared up 110 where lattice absorption starts K. Es wurden SrCl2-Einkristalle nach dem Czochralsky-Verfahren gezuchtet. Im Bereich bis Reflexionsmessiingen (bei K) und im Transmissionsmessungen 4,2 durchgefuhrt. Die irn Reflexionsspektrurn gefundene Reststrahlenbande nurde mittels klassischer Dispersionstheorie analysiert and, da eine befriedigende optimale Anpassung nicht zu erreichen war, zusatzlich einer Kraniers-Kronig-Analyse unterworfen. Es ergaben sich die Frequenzen der TO-Eigenschwingung LO-Mode 223 cm−1. taucht schon aus den Spektren von bekannte Schnlter auf, deren Ursache anhand Mehrphononenprozessen diskutiert wird. Ans Transmissionsrnessungen geht hervor, das SrCl2 fernen Infrarot durchlassig ist wo bei 4,2K Gitterscliwingungs-absorption einsetzt.