Mechanical properties of Y–Ba–Cu–O blocks welded by Er–Ba–Cu–O solder
作者： T Kaneko , K Iida , J Yoshioka , N Sakai , M Murakami
DOI: 10.1016/S0921-4534(03)00985-7
关键词:
摘要: Abstract In this study, we have performed the tensile tests of Y–Ba–Cu–O blocks welded by Er–Ba–Cu–O superconducting solder at room temperature. For comparative melt-textured and fabricated top-seeded melt growth are also tested. Most samples fractured joined region average strength was lower than those bulk samples. This is due to segregation foreign phases joint.
elsevier.com
sci-hub.se 参考文章(4)
A Murakami, K Katagiri, K Kasaba, Y Shoji, K Noto, N Sakai, M Murakami, Tensile strength and fracture surface topography of Sm-Ba-Cu-O bulk superconductors Superconductor Science and Technology. ,vol. 15, pp. 1099- 1104 ,(2002) , 10.1088/0953-2048/15/7/321
N Sakai, A Mase, H Ikuta, S-J Seo, U Mizutani, M Murakami, Mechanical properties of Sm-Ba-Cu-O/Ag bulk superconductors Superconductor Science and Technology. ,vol. 13, pp. 770- 773 ,(2000) , 10.1088/0953-2048/13/6/328
K Iida, J Yoshioka, N Sakai, M Murakami, Superconducting Joint of Y-Ba-Cu-O superconductors using Er-Ba-Cu-O solder Physica C-superconductivity and Its Applications. ,vol. 370, pp. 53- 58 ,(2002) , 10.1016/S0921-4534(01)01082-6
K Katagiri, A Murakami, T Sato, T Okudera, N Sakai, M Muralidhar, M Murakami, None, Stress-strain characteristics and fracture surface morphology of (Sm,Gd)-Ba-Cu-O bulk superconductor Physica C-superconductivity and Its Applications. ,vol. 378, pp. 722- 726 ,(2002) , 10.1016/S0921-4534(02)01529-0