Elastic-plastic finite element analysis of spall formation in gears
作者： Yan Ding , Rhys Jones , Bruce T. Kuhnell
DOI: 10.1016/0043-1648(96)06939-6
关键词:
摘要: Abstract This paper presents the results of an elastic-plastic finite element analysis behaviour subsurface cracks beneath pitch line a gear tooth. Attention is focused on potential for ligament collapse spalling mechanism as hypothesized by authors (Y. Ding, R. Jones and B.T. Kuhnell, Wear, 185 (1995) 141–149). The detailed numerical from this are compared with that previous linear elastic reported in above article, it shown qualitative agreement analysis.
elsevier.com
sci-hub.se 参考文章(21)
Donald C Stouffer, L T Damé, Inelastic Deformation of Metals: Models, Mechanical Properties, and Metallurgy ,(1996)
T.B. Kirk, G.W. Stachowiak, A.W. Batchelor, Fractal parameters and computer image analysis applied to wear particles isolated by ferrography Wear. ,vol. 145, pp. 347- 365 ,(1991) , 10.1016/0043-1648(91)90141-G
D.R. Wheeler, D.H. Buckley, Texturing in metals as a result of sliding Wear. ,vol. 33, pp. 65- 74 ,(1975) , 10.1016/0043-1648(75)90224-0
Ahmed Elkholy, Case depth requirements in carburized gears Wear. ,vol. 88, pp. 233- 244 ,(1983) , 10.1016/S0043-1648(83)80011-8
J. W. Blake, H. S. Cheng, A Surface Pitting Life Model for Spur Gears: Part I—Life Prediction Journal of Tribology-transactions of The Asme. ,vol. 113, pp. 712- 718 ,(1991) , 10.1115/1.2920683
H.-C. Sin, N. P. Suh, Subsurface Crack Propagation Due to Surface Traction in Sliding Wear Journal of Applied Mechanics. ,vol. 51, pp. 317- 323 ,(1984) , 10.1115/1.3167619
Yan Ding, Rhys Jones, Bruce Kuhnell, Numerical analysis of subsurface crack failure beneath the pitch line of a gear tooth during engagement Wear. ,vol. 185, pp. 141- 149 ,(1995) , 10.1016/0043-1648(95)06592-X
J.R. Fleming, N.P. Suh, Mechanics of crack propagation in delamination wear Wear. ,vol. 44, pp. 39- 56 ,(1977) , 10.1016/0043-1648(77)90083-7
S. Jahanmir, N.P. Suh, E.P. Abrahamson, Microscopic observations of the wear sheet formation by delamination Wear. ,vol. 28, pp. 235- 249 ,(1974) , 10.1016/0043-1648(74)90164-1
M. Kaneta, Y. Murakami, T. Okazaki, Growth Mechanism of Subsurface Crack Due to Hertzian Contact Journal of Tribology-transactions of The Asme. ,vol. 108, pp. 134- 139 ,(1986) , 10.1115/1.3261133