摘要: AbstractMetallographic examination performed on a number of micropitted gears has revealed microstructural features similar to those reported in the literature fatigued bearings, namely, dark etching regions and white bands. In addition, new type fatigue-induced constituent was observed close surface below asperities referred as plastic deformation region. Finally, it is shown that initiation propagation cracks leading formation micropits are related phase transformations mentioned previously.
sagepub.com
sci-hub.se 参考文章(40)
Adrian Oila, Micropitting and related phenomena in case carburised gears Newcastle University. ,(2003)
A. B. Jones, Metallographic Observations of Ball Bearing Fatigue Phenomena ASTM International. ,(1947) , 10.1520/STP42598S
A.V. Olver, H.A. Spikes, A.F. Bower, K.L. Johnson, The residual stress distribution in a plastically deformed model asperity Wear. ,vol. 107, pp. 151- 174 ,(1986) , 10.1016/0043-1648(86)90025-6
A. F. Bower, The influence of crack face friction and trapped fluid on surface initiated rolling contact fatigue cracks Journal of Tribology-transactions of The Asme. ,vol. 110, pp. 704- 711 ,(1988) , 10.1115/1.3261717
A. P. Voskampk, E. J. Mittemeijer, Crystallographic preferred orientation induced by cyclic rolling contact loading Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 27, pp. 3445- 3465 ,(1996) , 10.1007/BF02595437
Ragnar Österlund, Olof Vingsbo, Phase changes in fatigued ball bearings Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 11, pp. 701- 707 ,(1980) , 10.1007/BF02661199
S. Glodež, Z. Ren, J. Flašker, Surface fatigue of gear teeth flanks Computers & Structures. ,vol. 73, pp. 475- 483 ,(1999) , 10.1016/S0045-7949(98)00251-X
V. Bhargava, G. T. Hahn, C. A. Rubin, Rolling contact deformation, etching effects, and failure of high-strength bearing steel Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 21, pp. 1921- 1931 ,(1990) , 10.1007/BF02647240
S Glodež, Z Ren, Modelling of crack growth under cyclic contact loading Theoretical and Applied Fracture Mechanics. ,vol. 30, pp. 159- 173 ,(1998) , 10.1016/S0167-8442(98)00053-6
H. Swahn, P. C. Becker, O. Vingsbo, Electron-microscope studies of carbide decay during contact fatigue in ball bearings Metal science. ,vol. 10, pp. 35- 39 ,(1976) , 10.1179/030634576790431444