Production of Nanosized Boron Oxide Powder by High-Energy Ball Milling
作者： Mohammad Alizadeh , Fariborz Sharifianjazi , Ehsan Haghshenasjazi , Masood Aghakhani , Laleh Rajabi
DOI: 10.1080/15533174.2013.797438
关键词:
摘要: In this research, an attempt has been made to modify the microsized B2O3 powder into nanosized using ball mill. The sample was taken out after various hours of milling and it characterized for crystallite size. size >100, 30, 19 nm in 0, 1, 5 h time, respectively. experimental results showed that nanostructure particles total duration range 24–95 nm. shape milled round surface morphology is rough.
researchgate.net 
sci-hub.se 参考文章(17)
Yeon Hwang, Jong Kook Lee, Preparation of TiB2 powders by mechanical alloying Materials Letters. ,vol. 54, pp. 1- 7 ,(2002) , 10.1016/S0167-577X(01)00526-2
G.K Williamson, W.H Hall, X-ray line broadening from filed aluminium and wolfram Acta Metallurgica. ,vol. 1, pp. 22- 31 ,(1953) , 10.1016/0001-6160(53)90006-6
V.V. Dabhade, T.R. Rama Mohan, P. Ramakrishnan, Synthesis of nanosized titanium powder by high energy milling Applied Surface Science. ,vol. 182, pp. 390- 393 ,(2001) , 10.1016/S0169-4332(01)00456-1
E. Mohammad Sharifi, F. Karimzadeh, M.H. Enayati, A study on mechanochemical behavior of B2O3–Al system to produce alumina-based nanocomposite Journal of Alloys and Compounds. ,vol. 482, pp. 110- 113 ,(2009) , 10.1016/J.JALLCOM.2009.04.051
Cury Suryanarayana, Mechanical Alloying And Milling ,(2004)
S Abedini, N Parvin, P Ashtari, F S Jazi, Microstructure, strength and CO2 separation characteristics of α-alumina supported γ-alumina thin film membrane Advances in Applied Ceramics. ,vol. 112, pp. 17- 22 ,(2013) , 10.1179/1743676112Y.0000000043
Morteza Alizadeh, M.H. Paydar, F. Sharifian Jazi, Structural evaluation and mechanical properties of nanostructured Al/B4C composite fabricated by ARB process Composites Part B-engineering. ,vol. 44, pp. 339- 343 ,(2013) , 10.1016/J.COMPOSITESB.2012.04.069
S.S. Nayak, M. Wollgarten, J. Banhart, S.K. Pabi, B.S. Murty, Nanocomposites and an extremely hard nanocrystalline intermetallic of Al–Fe alloys prepared by mechanical alloying Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 527, pp. 2370- 2378 ,(2010) , 10.1016/J.MSEA.2009.12.044
E. Haghshenas Jazi, R. Esalmi-Farsani, Gh. Borhani, F. Sharifian Jazi, Synthesis and Characterization of In Situ Al-Al13Fe4-Al2O3-TiB2 Nanocomposite Powder by Mechanical Alloying and Subsequent Heat Treatment Synthesis and Reactivity in Inorganic Metal-organic and Nano-metal Chemistry. ,vol. 44, pp. 177- 184 ,(2014) , 10.1080/15533174.2013.768660
E. Haghshenas Jazi, G. Borhani, R. Esalmi Farsani, Preparation of Al-Fe/TiB 2 nanocomposite powder by ball milling and subsequent heat treatment Micro & Nano Letters. ,vol. 7, pp. 448- 452 ,(2012) , 10.1049/MNL.2012.0082