Cascade damage formation in gold under self-ion irradiation
作者： N. Sekimura , Y. Kanzaki , S.R. Okada , T. Masuda , S. Ishino
DOI: 10.1016/0022-3115(94)90048-5
关键词:
摘要: Abstract To understand cascade damage formation as a function of primary recoil energy, thin foils gold were irradiated with 20–400 keV self-ions to fluence 1.0 × 10 14 ions/m 2 at 300 K. The yield groups vacancy clusters per ion saturated an energy higher than 100 keV. number in group was found vary even for the same ions. size distribution not strongly dependent on and energy. An attempt made predict defect MeV neutrons from present data based spectrum.
harvard.edu
elsevier.com
sci-hub.se 参考文章(11)
S. Ishino, N. Sekimura, K. Hirooka, T. Muroga, In-situ observation of cascade damage in gold under heavy ion irradiation at high temperature Journal of Nuclear Materials. pp. 776- 780 ,(1986) , 10.1016/0022-3115(86)90091-7
Hiroyuki Sakaida, Naoto Sekimura, Shiori Ishino, In-situ observation of cascade damage in nickel and copper under heavy ion irradiation Journal of Nuclear Materials. ,vol. 179-181, pp. 928- 930 ,(1991) , 10.1016/0022-3115(91)90241-X
Naoto Sekimura, Shiori Ishino, Stability of cascade clusters in gold under energetic heavy ion irradiation Journal of Nuclear Materials. pp. 1217- 1221 ,(1988) , 10.1016/0022-3115(88)90499-0
M. Kiritani, T. Yoshiie, S. Kojima, Y. Satoh, Recoil energy spectrum analysis and impact effect of cascade and subcascade in 14 mev d-t fusion neutron irradiated FCC metals Radiation Effects and Defects in Solids. ,vol. 113, pp. 75- 96 ,(1990) , 10.1080/10420159008213056
J.P. Biersack, L.G. Haggmark, A Monte Carlo computer program for the transport of energetic ions in amorphous targets Nuclear Instruments and Methods. ,vol. 174, pp. 257- 269 ,(1980) , 10.1016/0029-554X(80)90440-1
A. Y. Stathopoulos, The study of heavy-ion damage in pure copper Philosophical Magazine A. ,vol. 44, pp. 285- 308 ,(1981) , 10.1080/01418618108239534
M. Kiritani, H. Kato, M. Hoshino, H. Matsui, N. Matsunami, Self-ion irradiation of fcc metals to elucidate primary recoil energy dependence of defect structure development during neutron irradiation Journal of Nuclear Materials. ,vol. 191, pp. 1128- 1133 ,(1992) , 10.1016/0022-3115(92)90651-Z
K. L. Merkle, L. R. Singer, J. R. Wrobel, ENERGY DEPENDENCE OF CASCADE CLUSTER FORMATION IN GOLD Applied Physics Letters. ,vol. 17, pp. 6- 7 ,(1970) , 10.1063/1.1653249
Yurugi Kanzaki, Naoto Sekimura, Shiori Ishino, Accumulation processes of cascade damage under heavy ion irradiation Journal of Nuclear Materials. ,vol. 191, pp. 1119- 1122 ,(1992) , 10.1016/0022-3115(92)90649-6
N. Sekimura, S. Ishino, In situ observation of cascade damage under heavy ion irradiation Radiation Effects and Defects in Solids. ,vol. 124, pp. 109- 116 ,(1992) , 10.1080/10420159208219832