Strength properties of unidirectionally reinforced hybrid composites
作者： R. D. Maksimov , �. Z. Plume , V. M. Ponomarev
DOI: 10.1007/BF00611572
关键词:
摘要: Experiments were carried out with several types of unidirectionally reinforced hybrid composites (organic fiberglass plastic, organic carbon-reinforced boron-reinforced and carbon plastic) various ratios the volume content fibers in modes simple quasistatic loading. It is shown that strength examined materials plane stress state can be described phenomenologically by polynomial criterion components tensors surface depending on structural parameters. The result used to predict (carry interpolation calculations) above-mentioned within ranges reinforcing optimize selection type ratio composite taking into account specific requirements properties material structures.
springer.com
harvard.edu
sci-hub.se 参考文章(4)
G. M. Gunyaev, Polycomponent high-modulus composites Polymer Mechanics. ,vol. 13, pp. 685- 692 ,(1978) , 10.1007/BF00860318
R. D. Maksimov, �. Z. Plume, V. M. Ponomarev, Elasticity characteristics of unidirectionally reinforced hybrid composites Mechanics of Composite Materials. ,vol. 19, pp. 9- 15 ,(1983) , 10.1007/BF00604019
R. D. Maksimov, E. A. Sokolov, �. Z. Plume, Equilong-term strength surfaces of organic textolite in the plane stressed state Mechanics of Composite Materials. ,vol. 15, pp. 40- 45 ,(1979) , 10.1007/BF00604955
Edward M. Wu, Optimal Experimental Measurements of Anisotropic Failure Tensors Journal of Composite Materials. ,vol. 6, pp. 472- 489 ,(1972) , 10.1177/002199837200600304