Efficient grating-tuned mid-infrared Cr2+:CdSe laser.
作者： Jason McKay , Kenneth L. Schepler , Gary C. Catella
DOI: 10.1364/OL.24.001575
关键词:
摘要: Room-temperature, all-solid-state, broadly tunable laser operation of Cr2+-doped CdSe has been demonstrated. Pumping with a Q-switched Tm, Ho:YLF running at 1-kHz repetition rate achieved broadband output 500 mW 2.6 µm 48% absorbed power slope efficiency. With reduced efficiency, as much 815 was obtained. diffraction grating, the Cr2+:CdSe tuned from 2.3 to 2.9 µm 10-nm bandwidth (FWHM) and up 350 mW.
osapublishing.org参考文章(4)
U. Hömmerich, X. Wu, V. R. Davis, S. B. Trivedi, K. Grasza, R. J. Chen, S. Kutcher, Demonstration of room-temperature laser action at 2.5 µm from Cr 2+ :Cd 0.85 Mn 0.15 Te Optics Letters. ,vol. 22, pp. 1180- 1182 ,(1997) , 10.1364/OL.22.001180
K.L. Schepler, S. Kück, L. Shiozawa, Cr2+ emission spectroscopy in CdSe Journal of Luminescence. pp. 116- 117 ,(1997) , 10.1016/S0022-2313(97)00051-3
L.D. DeLoach, R.H. Page, G.D. Wilke, S.A. Payne, W.F. Krupke, Transition metal-doped zinc chalcogenides: spectroscopy and laser demonstration of a new class of gain media IEEE Journal of Quantum Electronics. ,vol. 32, pp. 885- 895 ,(1996) , 10.1109/3.502365
R.H. Page, K.I. Schaffers, L.D. DeLoach, G.D. Wilke, F.D. Patel, J.B. Tassano, S.A. Payne, W.F. Krupke, K.-T. Chen, A. Burger, Cr/sup 2+/-doped zinc chalcogenides as efficient, widely tunable mid-infrared lasers IEEE Journal of Quantum Electronics. ,vol. 33, pp. 609- 619 ,(1997) , 10.1109/3.563390