Shattered Rim and Shelling of High-Speed Railway Wheels in The Very-High-Cycle Fatigue Regime Under Rolling Contact Loading
作者： Tao Cong , Jianmin Han , Youshi Hong , Joseph P. Domblesky , Xiaolong Liu
DOI: 10.1016/J.ENGFAILANAL.2019.01.047
关键词:
摘要: … shattered rim and shelling are the main failure causes of the high-speed railway wheels. In this paper, shattered … years CRH operation indicated that all shattered rims and shelling were …
sci-hub.se 参考文章(30)
T. Sakai, N. Oguma, A. Morikawa, Microscopic and nanoscopic observations of metallurgical structures around inclusions at interior crack initiation site for a bearing steel in very high-cycle fatigue Fatigue & Fracture of Engineering Materials & Structures. ,vol. 38, pp. 1305- 1314 ,(2015) , 10.1111/FFE.12344
B. Alfredsson, J. Dahlberg, M. Olsson, The role of a single surface asperity in rolling contact fatigue Wear. ,vol. 264, pp. 757- 762 ,(2008) , 10.1016/J.WEAR.2006.11.055
Y. MURAKAMI, N. N. YOKOYAMA, J. NAGATA, Mechanism of fatigue failure in ultralong life regime Fatigue & Fracture of Engineering Materials & Structures. ,vol. 25, pp. 735- 746 ,(2002) , 10.1046/J.1460-2695.2002.00576.X
Anders Ekberg, Bengt Åkesson, Elena Kabo, Wheel/rail rolling contact fatigue – Probe, predict, prevent Wear. ,vol. 314, pp. 2- 12 ,(2014) , 10.1016/J.WEAR.2013.12.004
Y. Murakami, T. Nomoto, T. Ueda, Y. Murakami, On the mechanism of fatigue failure in the superlong life regime (N>107 cycles). Part 1: influence of hydrogen trapped by inclusions Fatigue & Fracture of Engineering Materials & Structures. ,vol. 23, pp. 893- 902 ,(2000) , 10.1046/J.1460-2695.2000.00328.X
Anders Ekberg, Elena Kabo, Jens C.O. Nielsen, Roger Lundén, Subsurface initiated rolling contact fatigue of railway wheels as generated by rail corrugation International Journal of Solids and Structures. ,vol. 44, pp. 7975- 7987 ,(2007) , 10.1016/J.IJSOLSTR.2007.05.022
P.J. Mutton, C.J. Epp, J. Dudek, Rolling contact fatigue in railway wheels under high axle loads Wear. ,vol. 144, pp. 139- 152 ,(1991) , 10.1016/0043-1648(91)90011-I
Anders Ekberg, Elena Kabo, Fatigue of railway wheels and rails under rolling contact and thermal loading—an overview Wear. ,vol. 258, pp. 1288- 1300 ,(2005) , 10.1016/J.WEAR.2004.03.039
Yongming Liu, Liming Liu, Sankaran Mahadevan, Analysis of subsurface crack propagation under rolling contact loading in railroad wheels using FEM Engineering Fracture Mechanics. ,vol. 74, pp. 2659- 2674 ,(2007) , 10.1016/J.ENGFRACMECH.2007.02.012
Taizo Makino, Miyuki Yamamoto, Takashi Fujimura, Effect of material on spalling properties of railroad wheels Wear. ,vol. 253, pp. 284- 290 ,(2002) , 10.1016/S0043-1648(02)00117-5