Reply to the “comment on ‘investigation on the 1000, 1150 and 1400 °C isothermal section of the TiAlNb system’ ”—Part II. Modification of 1000 and 1150 °C isothermal sections of the TiAlNb system
作者： Jin-Jun Ding , Shi-Ming Hao , None
DOI: 10.1016/S0966-9795(97)00080-0
关键词:
摘要: Abstract Some phase relationships in the 1000 and 1150 °C isothermal sections were further studied by bulk alloy method using four alloys. The existence of Gamma 1 is confirmed present EPMA X-ray diffraction results as well metallographic observations. at above two temperatures modified according to these experimental results.
elsevier.com
sci-hub.se 参考文章(6)
N.S. Stoloff, C.C. Koch, C.T. Liu, High-temperature ordered intermetallic alloys Materials Research Society,Pittsburgh, PA. ,(1985)
T.J Jewett, Comment on ‘Investigation on the 1000, 1150 and 1400°C isothermal section of the Ti-Al-Nb system’ Intermetallics. ,vol. 5, pp. 157- 159 ,(1997) , 10.1016/S0966-9795(96)00076-3
G.L. Chen, X.T. Wang, K.Q. Ni, S.M. Hao, J.X. Cao, J.J. Ding, X. Zhang, Investigation on the 1000, 1150 and 1400 °C isothermal section of the TiAlNb system Intermetallics. ,vol. 4, pp. 13- 22 ,(1996) , 10.1016/0966-9795(95)00012-N
V. R. Parameswaran, High temperature aluminides and intermetallics JOM. ,vol. 44, pp. 41- 43 ,(1992) , 10.1007/BF03222254
A Quye, S Charters, Richard P Evershed, Mat Res Soc Symp Proc Cambridge University Press. ,(1995)
J. Zhu, X. X. Zhang, M. Knobel, R. H. Yu, Cobalt rich phase formation in metastable Cu–Co alloys by means of melt spinning Materials Science and Technology. ,vol. 12, pp. 464- 468 ,(1996) , 10.1179/MST.1996.12.6.464