Pore Structure of Calcium Silicate Hydrate in Hydrated Tricalcium Silicate
作者： MASAKI DAIMON , SALAH A. ABO-EL-ENEIN , GIRO ROSARA , SEISHI GOTO , RENICHI KONDO
DOI: 10.1111/J.1151-2916.1977.TB15483.X
关键词:
摘要: Adsorption of N2 and water vapor was studied in completely hydrated tricalcium silicate fully from which Ca(OH)2 had been extracted. Compared with results obtained using N2, adsorption led to increased values for small-pore volume, peak shifts smaller sizes, decreased large-pore volume. Marked hysteresis observed the case adsorption; resorption branch apparently represents true pore structure. Extraction paste calculated volume small pores strikingly, suggesting that is hindered by Ca(OH)2; this tendency more obvious adsorption. The measurements indicate existence two kinds pores, i.e. a wider intergel-particle existing within gel particle. latter further classified into intercrystallite intracrystallite pores.
sci-hub.se 参考文章(11)
Julius Hagymassy, Stephen Brunauer, R.Sh Mikhail, Pore structure analysis by water vapor adsorption: I. t-Curves for water vapor Journal of Colloid and Interface Science. ,vol. 29, pp. 485- 491 ,(1969) , 10.1016/0021-9797(69)90132-5
R.F. Feldman, V.S. Ramachandran, Differentiation of interlayer and adsorbed water in hydrated portland cement by thermal analysis Cement and Concrete Research. ,vol. 1, pp. 607- 620 ,(1971) , 10.1016/0008-8846(71)90016-0
Jan Skalny, Ivan Odler, Pore structure of calcium silicate hydrates Cement and Concrete Research. ,vol. 2, pp. 387- 400 ,(1972) , 10.1016/0008-8846(72)90055-5
R. Sh. Mikhail, A. M. Kamel, S. A. Abo-El-Enein, Surface properties of cement hydration products. I. Pore structure of calcium silicate hydrates prepared in a suspension form Journal of Chemical Technology & Biotechnology. ,vol. 19, pp. 324- 328 ,(2007) , 10.1002/JCTB.5010191105
R.F. Feldman, V.S. Ramachandran, Modified thermal analysis equipment and technique for study under controlled humidity conditions Thermochimica Acta. ,vol. 2, pp. 393- 403 ,(1971) , 10.1016/0040-6031(71)85015-3
Renichi Kondo, Salah A. Abo-El-Enein, Masaki Daimon, Kinetics and Mechanisms of Hydrothermal Reaction of Granulated Blast Furnace Slag Bulletin of the Chemical Society of Japan. ,vol. 48, pp. 222- 226 ,(1975) , 10.1246/BCSJ.48.222
R. F. Feldman, P. J. Sereda, A model for hydrated Portland cement paste as deduced from sorption-length change and mechanical properties Matériaux et Constructions. ,vol. 1, pp. 509- 520 ,(1968) , 10.1007/BF02473639
Stephen Brunauer, Marvin Yudenfreund, Ivan Odler, Jan Skalny, Hardened portland cement pastes of low porosity VI. Mechanism of the hydration process Cement and Concrete Research. ,vol. 3, pp. 129- 147 ,(1973) , 10.1016/0008-8846(73)90043-4
Stephen Brunauer, R.Sh Mikhail, E.E Bodor, Pore structure analysis without a pore shape model Journal of Colloid and Interface Science. ,vol. 24, pp. 451- 463 ,(1967) , 10.1016/0021-9797(67)90243-3
D.L Kantro, Stephen Brunauer, C.H Weise, The ball-mill hydration of tricalcium silicate at room temperature Journal of Colloid Science. ,vol. 14, pp. 363- 376 ,(1959) , 10.1016/0095-8522(59)90001-7