AE およびラマン分光による Cr2O3 皮膜のその場剥離評価
作者： Yoshitaka Nishiyama , Kazuyuki Kitamura , Takeo Kudo , Nobuo Otsuka
关键词:
摘要: … and Raman spectroscopy were applied to measure in situ oxide spallation during cooling. The AE signal was detected during a temperature decrease due to fracture of a Cr2O3 … Raman …
sci-hub.se 参考文章(24)
Shigeji Taniguchi, Takashi Furukawa, Toshio Shibata, Failure of scales formed on Cu-containing low carbon steels during cooling Isij International. ,vol. 37, pp. 263- 271 ,(1997) , 10.2355/ISIJINTERNATIONAL.37.263
Michael Schütze, Protective oxide scales and their breakdown ,(1997)
Kenneth R Lawless, Allan T Gwathmey, The structure of oxide films on different faces of a single crystal of copper Acta Metallurgica. ,vol. 4, pp. 153- 163 ,(1956) , 10.1016/0001-6160(56)90133-X
Anders Norin, Mechanical stresses developed in austenitic Fe-Cr-Ni alloys by oxidation in a CO2 atmosphere Oxidation of Metals. ,vol. 9, pp. 259- 274 ,(1975) , 10.1007/BF00613276
W. Christi, A. Rahmel, M. Sch�tze, Behavior of oxide scales on 2.25Cr-1Mo steel during thermal cycling. I. Scales formed in oxygen and air Oxidation of Metals. ,vol. 31, pp. 1- 34 ,(1989) , 10.1007/BF00665485
J Birnie, C Craggs, D.J Gardiner, P.R Graves, Ex situ and in situ determination of stress distributions in chromium oxide films by raman microscopy Corrosion Science. ,vol. 33, pp. 1- 12 ,(1992) , 10.1016/0010-938X(92)90014-T
J. Robertson, M. I. Manning, Limits to adherence of oxide scales Materials Science and Technology. ,vol. 6, pp. 81- 92 ,(1990) , 10.1179/MST.1990.6.1.81
Kazuyuki Kitamura, Yoshitaka Nishiyama, Nobuo Otsuka, T. Kudo, In Situ Growth-Stress Measurement of Cr2O3 Scale Formed on Stainless Steels by Raman Spectroscopy Materials Science Forum. pp. 489- 496 ,(2006) , 10.4028/WWW.SCIENTIFIC.NET/MSF.522-523.489
R. E. Pawel, J. V. Cathcart, J. J. Campbell, Stress Generation in Tantalum During Oxidation Journal of The Electrochemical Society. ,vol. 110, pp. 551- 557 ,(1963) , 10.1149/1.2425812
D. Delaunay, A.M. Huntz, P. Lacombe, Mechanical stresses developed in high temperature resistant alloys during isothermal and cyclic oxidation treatments: The influence of yttrium additions on oxide scale adherence Corrosion Science. ,vol. 20, pp. 1109- 1117 ,(1980) , 10.1016/0010-938X(80)90141-9