Investigation on oxygen controlled liquid lead corrosion of surface treated steels
作者： G Müller , G Schumacher , F Zimmermann
DOI: 10.1016/S0022-3115(99)00211-1
关键词:
摘要: Abstract A low alloyed martensitic steel Fe9Cr (OPTIFER IVc) and an austenitic 16Cr15Ni (1.4970) were exposed to liquid lead examine their suitability as structural material for cooled accelerator driven subcritical actinide burners. The surface of part the specimens was restructured that another with Al by treatment high power pulsed electron beams. corrosion test stand constructed containing under oxygen control at 550°C. Steel examined after 800, 1500 3000 h exposure. For lower effects observed especially when treated beam. No attack could be seen all on both steels alloying into a layer 10 μm depth.
harvard.edu
elsevier.com
sci-hub.se 参考文章(12)
B. F. Gromov, Yu. I. Orlov, P. N. Martynov, K. D. Ivanov, V. A. Gulevsky, Physical — Chemical Principles of Lead — Bismuth Coolant Technology Springer, Boston, MA. pp. 339- 343 ,(1995) , 10.1007/978-1-4615-1977-5_37
S. K. Mitra, S. K. Roy, S. K. Bose, Improvement of nonisothermal oxidation behavior of fe and fe-cr alloys by superficially applied reactive oxide coatings Oxidation of Metals. ,vol. 34, pp. 101- 121 ,(1990) , 10.1007/BF00664341
Nicolas Fiétier, J.A. Rubio, F. Carminati, P. Mandrillon, J. Galvez, R. Klapisch, S. Buono, Ch. Roche, C. Rubbia, C. Gelès, J.P. Revol, Y. Kadi, Conceptual design of a fast neutron operated high power energy amplifier Energia nucleare. ,vol. 13, pp. 3- 104 ,(1995)
Rodney P. Elliott, Max Hansen, Kurt Anderko, Constitution of binary alloys, first supplement McGraw-Hill. ,(1965)
Carlo Rubbia, A high gain energy amplifier operated with fast neutrons The International Conference on accelerator-driven transmutation technologies and Applications. ,vol. 346, pp. 44- 53 ,(1995) , 10.1063/1.49069
G Müller, G Schumacher, D Strauß, Oxide scale growth on MCrAlY coatings after pulsed electron beam treatment Surface & Coatings Technology. pp. 43- 47 ,(1998) , 10.1016/S0257-8972(98)00631-8
H.U Borgstedt, H Glasbrenner, Development of a direct insulation layer for a self-cooled liquid metal fusion reactor blanket Fusion Engineering and Design. ,vol. 27, pp. 659- 662 ,(1995) , 10.1016/0920-3796(95)90181-7
R.C. Asher, D. Davies, S.A. Beetham, Some observations on the compatibility ofstructural materials with molten lead Corrosion Science. ,vol. 17, pp. 545- 557 ,(1977) , 10.1016/S0010-938X(77)80001-2
G. Y. Lai, High Temperature Corrosion of Engineering Alloys ,(1990)
K. Kuroda, P. A. Labun, G. Welsch, T. E. Mitchell, Oxide-formation characteristics in the early stages of oxidation of Fe and Fe-Cr alloys Oxidation of Metals. ,vol. 19, pp. 117- 127 ,(1983) , 10.1007/BF01225979