Dislocation etch pits in silicon iron
作者： J.G Suits , J.R Low
DOI: 10.1016/0001-6160(57)90103-7
关键词:
摘要: Abstract It has been demonstrated that the segregation of carbon to dislocation sites is a necessary pre-requisite production etch pits in slip bands silicon ferrite. In regions heavy deformation, etch-pitting may not be observed if content material too low; such at produced increased by low-temperature earburization.
elsevier.com
sci-hub.se 参考文章(7)
F. L. Vogel, W. G. Pfann, H. E. Corey, E. E. Thomas, Observations of Dislocations in Lineage Boundaries in Germanium Physical Review. ,vol. 90, pp. 489- 490 ,(1953) , 10.1103/PHYSREV.90.489
C.G. Dunn, W.R. Hibbard, Some observations of dislocation sites in polygonized silicon-iron crystals Acta Metallurgica. ,vol. 3, pp. 409- 411 ,(1955) , 10.1016/0001-6160(55)90047-X
J.F Nye, Some geometrical relations in dislocated crystals Acta Metallurgica. ,vol. 1, pp. 153- 162 ,(1953) , 10.1016/0001-6160(53)90054-6
S. Amelinckx, Slip lines and etchpits Philosophical Magazine Series 1. ,vol. 44, pp. 1048- 1049 ,(1953) , 10.1080/14786440908521073
G. Wyon, J.M. Marchin, CXXIV. Formation of etch pits on slip lines in aluminium Philosophical Magazine Series 1. ,vol. 46, pp. 1119- 1122 ,(1955) , 10.1080/14786441008521124
W. T. Read, W. Shockley, Dislocation Models of Crystal Grain Boundaries Physical Review. ,vol. 78, pp. 275- 289 ,(1950) , 10.1103/PHYSREV.78.275
R. Gevers, Observations microscopiques et interferométriques de figures de corrosion, et leur interprétation à l'aide des dislocations Journal de Chimie Physique. ,vol. 50, pp. 321- 328 ,(1953) , 10.1051/JCP/1953500321