Composition and Microstructure of 20-year-old Ordinary Portland Cement-ground Granulated Blast-furnace Slag Blends Containing 0 to 100% Slag
作者： R. Taylor , I.G. Richardson , R.M.D. Brydson
DOI: 10.1016/J.CEMCONRES.2010.02.012
关键词:
摘要: … increasing slag content, and the Al/Si ratio increased. The Ca/Si ratio of C–S–H in the slag-… and the amount of Ca(OH) 2 was reduced indicating that additional slag must have reacted. …
elsevier.com
sci-hub.se 参考文章(36)
Ivan Klur, Benoît Pollet, Joseph Virlet, André Nonat, C-S-H Structure Evolution with Calcium Content by Multinuclear NMR Nuclear Magnetic Resonance Spectroscopy of Cement-Based Materials. pp. 119- 141 ,(1998) , 10.1007/978-3-642-80432-8_8
Donald E. Woessner, Characterization of clay minerals by 22 Al nuclear magnetic resonance spectroscopy American Mineralogist. ,vol. 74, pp. 203- 215 ,(1989)
J. A. Chudek, G. Hunter, M. R. Jones, S. N. Scrimgeour, P. C. Hewlett, A. B. Kudryavtsev, Aluminium-27 solid state NMR spectroscopic studies of chloride binding in Portland cement and blends Journal of Materials Science. ,vol. 35, pp. 4275- 4288 ,(2000) , 10.1023/A:1004824100029
I. G RICHARDSON, G. W GROVES, The structure of the calcium silicate hydrate phases present in hardened pastes of white Portland cement/blast-furnace slag blends Journal of Materials Science. ,vol. 32, pp. 4793- 4802 ,(1997) , 10.1023/A:1018639232570
Mark E. Smith, Kenneth J. D. MacKenzie, Multinuclear solid-state NMR of inorganic materials Pergamon. ,(2002)
A. V. Girao, I. G. Richardson, C. B. Porteneuve, R. M. D. Brydson, morphology and nanostructure C–S–H in white Portland cement–fly ash hydrated at 85°C Advances in Applied Ceramics. ,vol. 106, pp. 283- 293 ,(2007) , 10.1179/174367607X228098
Robert C. T. Slade, Jennifer C. Southern, Ian M. Thompson, 27Al nuclear magnetic resonance spectroscopy investigation of thermal transformation sequences of alumina hydrates. Part 1.—Gibbsite, γ-Al(OH)3 J. Mater. Chem.. ,vol. 1, pp. 563- 568 ,(1991) , 10.1039/JM9910100563
I.G. Richardson, Tobermorite/jennite- and tobermorite/calcium hydroxide-based models for the structure of C-S-H: applicability to hardened pastes of tricalcium silicate, β-dicalcium silicate, Portland cement, and blends of Portland cement with blast-furnace slag, metakaolin, or silica fume Cement and Concrete Research. ,vol. 34, pp. 1733- 1777 ,(2004) , 10.1016/J.CEMCONRES.2004.05.034
I.G. Richardson, G.W. Groves, The incorporation of minor and trace elements into calcium silicate hydrate (CSH) gel in hardened cement pastes Cement and Concrete Research. ,vol. 23, pp. 131- 138 ,(1993) , 10.1016/0008-8846(93)90143-W
R. Taylor, I. G. Richardson, R. M. D. Brydson, Nature of C–S–H in 20 year old neat ordinary Portland cement and 10% Portland cement–90% ground granulated blast furnace slag pastes Advances in Applied Ceramics. ,vol. 106, pp. 294- 301 ,(2007) , 10.1179/174367607X228106