Dissolution Condensation Mechanism of Stress Corrosion Cracking in Liquid Metals: Driving Force and Crack Kinetics
作者： Evgeny E. Glickman
DOI: 10.1007/S11661-010-0429-6
关键词:
摘要: … the equilibrium solubility C ∞ (T) of the metal ions and their diffusivity D L in the corrosive liquid… of repassivation, it should relate to the corrosion products formed here. The crack kinetics …
harvard.edu
springer.com
sci-hub.se 参考文章(35)
A.R.C. Westwood, C.M. Preece, M.H. Kamdar, ADSORPTION-INDUCED BRITTLE FRACTURE IN LIQUID-METAL ENVIRONMENTS pp 589-644 of Fracture. An Advanced Treatise. Vol. III. / Liebowitz, H. (ed.). New York Academic Press Inc. (1971).. pp. 589- 644 ,(1971) , 10.1016/B978-0-12-449703-0.50015-1
E.E. Glickman, Grain Boundary Grooving Accelerated by Local Plasticity as a Possible Mechanism of Liquid Metal Embrittlement Interface Science. ,vol. 11, pp. 451- 459 ,(2003) , 10.1023/A:1026100112248
S.K. Banerji, C.L. Briant, Embrittlement, Engineering Alloys Encyclopedia of Physical Science and Technology. pp. 407- 432 ,(2003) , 10.1016/B0-12-227410-5/00221-0
R. B. Heimann, Auflösung von Kristallen : Theorie und technische Anwendung Springer-Verlag. ,(1975)
Wolfgang Gust, Yuri. Mishin, Inderjeet Kaur., Fundamentals of grain and interphase boundary diffusion ,(1995)
T.L. Anderson, Fracture Mechanics : Fundamentals and Applications NASA STI/Recon Technical Report A. ,vol. 92, pp. 40200- ,(2017) , 10.1201/9781315370293
S.P. Lynch, Solid-metal-induced embrittlement of aluminium alloys and other materials Materials Science and Engineering: A. ,vol. 108, pp. 203- 212 ,(1989) , 10.1016/0921-5093(89)90421-8
Z. Hadjem-Hamouche, T. Auger, I. Guillot, Temperature effect in the maximum propagation rate of a liquid metal filled crack: The T91 martensitic steel/Lead–Bismuth Eutectic system Corrosion Science. ,vol. 51, pp. 2580- 2587 ,(2009) , 10.1016/J.CORSCI.2009.06.049
C. L. Briant, Metallurgical Aspects of Environmental Failures ,(1985)
R.N. Stevens, R. Dutton, The propagation of Griffith cracks at high temperatures by mass transport processes Materials Science and Engineering. ,vol. 8, pp. 220- 234 ,(1971) , 10.1016/0025-5416(71)90076-0