摘要: Abstract The misch metal-iron (MM-Fe) system has been investigated in the temperature range from 700 to 1150 °C at iron-rich end (up 33.3% RE, where RE is total rare earth content of MM). Two intermediate phases, Fe 17 2 and two broad three-phase fields, α - + liquid , exist region MM-Fe system. γ-Fe phase cannot be retained by quenching alloys high temperature. solid solubility iron less than 0.5 at.%.
sci-hub.se 参考文章(5)
M.Uma Devi, K.P Gupta, Phase equilibria in the REFeB system at 1000 °C Journal of the Less Common Metals. ,vol. 159, pp. 13- 21 ,(1990) , 10.1016/0022-5088(90)90127-6
Y.C. Chuang, C.H. Wu, Z.B. Shao, Investigation of the CeFe binary system Journal of the Less Common Metals. ,vol. 136, pp. 147- 153 ,(1987) , 10.1016/0022-5088(87)90018-X
Thaddeus B Massalski, Hiroaki Okamoto, PRnbsp Subramanian, Linda Kacprzak, William W Scott, None, Binary alloy phase diagrams ASM International. ,vol. 3, pp. 2874- ,(1986)
Gerhard Schneider, Fernando JG Landgraf, Frank P Missell, None, Additional ferromagnetic phases in the FeNdB system and the effect of a 600°C annealing Journal of The Less Common Metals. ,vol. 153, pp. 169- 180 ,(1989) , 10.1016/0022-5088(89)90543-2
Fernando JG Landgraf, Gerhard S Schneider, Valquíria Villas-Boas, Frank P Missell, None, Solidification and solid state transformations in FeNd: A revised phase diagram Journal of the Less Common Metals. ,vol. 163, pp. 209- 218 ,(1990) , 10.1016/0022-5088(90)90101-O