Misfit analysis in lamellar microstructure in NbSi2/MoSi2 duplex crystals
作者： Vaclav Paidar , Takayoshi Nakano
DOI: 10.1016/J.JALLCOM.2014.04.025
关键词:
摘要: Abstract Recent experimental investigation of additional alloying pseudobinary (Mo(1−x)Nbx)Si2 disilicides showed surprisingly a similar effect smaller and larger atoms (chromium zirconium) on the interface misfit. Nevertheless, it is shown in this short paper that measured modifications misfit at interfaces between C11b C40 lattices two-phase systems transition metal can be agreement with or calculated values lattice parameters pure binary systems.
elsevier.com
sci-hub.se 参考文章(6)
H.J. Goldschmidt, J.A. Brand, The constitution of the chromium-niobium-silicon system Journal of The Less Common Metals. ,vol. 3, pp. 34- 43 ,(1961) , 10.1016/0022-5088(61)90041-8
T. Nakano, M. Azuma, Y. Umakoshi, Microstructure and high-temperature strength in duplex silicides Intermetallics. ,vol. 6, pp. 715- 722 ,(1998) , 10.1016/S0966-9795(98)00054-5
A.K. Vasudévan, J.J. Petrovic, A comparative overview of molybdenum disilicide composites Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 155, pp. 1- 17 ,(1992) , 10.1016/0921-5093(92)90308-N
Koji Hagihara, Yoichiro Hama, Koretaka Yuge, Takayoshi Nakano, Misfit strain affecting the lamellar microstructure in NbSi2/MoSi2 duplex crystals Acta Materialia. ,vol. 61, pp. 3432- 3444 ,(2013) , 10.1016/J.ACTAMAT.2013.02.035
T. Nakano, Y. Nakai, S. Maeda, Y. Umakoshi, Microstructure of duplex-phase NbSi2(C40)/MoSi2(C11b) crystals containing a single set of lamellae Acta Materialia. ,vol. 50, pp. 1781- 1795 ,(2002) , 10.1016/S1359-6454(02)00030-7
O. Thomas, J.P. Senateur, R. Madar, O. Laborde, E. Rosencher, Molybdenum disilicide: Crystal growth, thermal expansion and resistivity Solid State Communications. ,vol. 55, pp. 629- 632 ,(1985) , 10.1016/0038-1098(85)90827-0