Structural Materials for Nuclear Power Plants
作者： SF Etris , YR Fiorni , KC Lieb , IC Moore , AL Batik
DOI: 10.1520/JTE11676J
关键词:
摘要: Commercial ferritic and austenitic steels are the predominant materials used in both fossil nuclear power plants; significant difference plants is exposure to neutron fluence. Three aspects of material behavior reviewed: (1) role residual elements on radiation damage for water reactor pressure vessels, (2) influence neutron-gamma flux coolant stress corrosion, (3) neutron-induced swelling void formation stainless fast reactors. (auth)
osti.gov
sci-hub.st 参考文章(15)
F. A. Smidt, H. E. Watson, Effect of residual elements on radiation strengthening in iron alloys, pressure vessel steels, and welds Met. Trans. 3: No. 8, 2065-73 (Aug 1972).. ,vol. 3, pp. 2065- 2073 ,(1972) , 10.1007/BF02643215
W. N. McElroy, C. Z. Serpan, DAMAGE-FUNCTION ANALYSIS OF NEUTRON-ENERGY AND SPECTRUM EFFECTS UPON THE RADIATION EMBRITTLEMENT OF STEELS. pp 33-51 of Radiation Damage in Reactor Materials. Vol. II. Vienna International Atomic Energy Agency (1969).. ,(1969)
J. R. Hawthorne, L. E. Steele, In-Reactor Studies of Low-Cycle Fatigue Properties of a Nuclear Pressure Vessel Steel ASTM International. ,(1965) , 10.1520/STP43539S
F.A. Smidt, J.A. Sprague, Suppression of void nucleation by a vacancy trapping mechanism Scripta Metallurgica. ,vol. 7, pp. 495- 501 ,(1973) , 10.1016/0036-9748(73)90102-6
F.J Loss, Effect of mechanical constraint on the fracture characteristics of thick-section steel Nuclear Engineering and Design. ,vol. 17, pp. 16- 31 ,(1971) , 10.1016/0029-5493(71)90037-9
D. I. R. Norris, VOIDS IN IRRADIATED METALS. PART I. Radiation Effects and Defects in Solids. ,vol. 15, pp. 1- 22 ,(1972) , 10.1080/00337577208230470
F.J. Witt, T.R. Mager, Fracture toughness values at temperatures up to 550°F for astm A 533 grade B, class 1 steel Nuclear Engineering and Design. ,vol. 17, pp. 91- 102 ,(1971) , 10.1016/0029-5493(71)90042-2
T.R. Mager, Fracture toughness properties of heavy section A533, grade B, class 1 steel plate and submerged arc weldment Nuclear Engineering and Design. ,vol. 17, pp. 76- 90 ,(1971) , 10.1016/0029-5493(71)90041-0
J.R. Hawthorne, Postirradiation dynamic tear and Charpy-V performance of 12-in. thick A533-B steel plates and weld metal Nuclear Engineering and Design. ,vol. 17, pp. 116- 130 ,(1971) , 10.1016/0029-5493(71)90044-6
P. G. Shewmon, Radiation-induced swelling of stainless steel. Science. ,vol. 173, pp. 987- 991 ,(1971) , 10.1126/SCIENCE.173.4001.987